Eastman 1810A Polyethylene (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Eastman 1810A Polyethylene (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyethylene 1810A contains no additives. It is suggested for injection molding applications.Information from manufacturer data sheet.Eastman Chemical Company sold its polyethylene business to Westlake Chemical Corporation in Dec. 2006. This grade no longer appears in the Westlake product line.

Physical Properties	Metric	English	Comments
Density	0.921 g/cc	0.0333 lb/in³	ASTM D 4883
Melt Flow	0.70 g/10 min @Load 2.16 kg, Temperature 190 °C	0.70 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	13.8 MPa	2000 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Tensile Strength, Yield	11.0 MPa	1600 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Elongation at Break	500 %	500 %	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Flexural Modulus	0.221 GPa	32.1 ksi	2% Secant, 12.7 mm/min. (0.5 in./min.); ASTM D790

Thermal Properties	Metric	English	Comments
Vicat Softening Point	95.0 °C	203 °F	ASTM D1525
Brittleness Temperature	<= -73.0 °C	<= -99.4 °F	ASTM D746

Descriptive Properties	Value	Comments
Process	Injection