Polymer Property : Flexural Yield Strength = 19600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	135 MPa	19600 psi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Nemcon™ H PK DP110/X5 Polyetheretherketone Thermally Conductive Polyetheretherketone, excellent chemical, high stiffness, modulus and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All sa..
Flexural Yield Strength	135 MPa	19600 psi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Opnyl OP66GF15 Nylon 66, 14% Glass Reinforced Nylon 66 - Glass reinforced (14 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared..
Flexural Yield Strength	135 MPa	19600 psi	DIN 53 452
Albis Plastics Tedur® L V 9900-1 PPS, Unreinforced (discontinued **) Excellent Surface Finish, High Chemical Resistance. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Pipes, ProfilesProcessing: Extrusion (Melt Temperature: 555-610°F)..
Flexural Yield Strength	135 MPa	19600 psi	ASTM Data
BASF Capron® 5202 HS BK-102 Nylon 66 (Dry) (discontinued **) Capron 5202 HS BK-102 is an unfilled, heat stabilized, pigmented black nylon 6,6, injection molding compound. It combines strength and stiffness as well as excellent chemical resistance. The additi..
Flexural Yield Strength	135 MPa @Strain 3.50 %	19600 psi @Strain 3.50 %	d.a.m., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 20 FN20 DUS013 000000 Nylon 6, 20% Glass Fiber PA 6, 20% glass fibers, injection molding, halogen-free flame retardantInformation provided by LANXESS.
Flexural Yield Strength	135 MPa	19600 psi	ASTM D790
Lucky CH-910 Acrylic, Coextrusion Grade Coextrusion grade. May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistance, excellent chemical resistance and coloring capability.
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem 2212 PEI (Europe-Africa-Middle East) 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2212R PEI (Europe-Africa-Middle East) 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. Resin is RoHS compliant. UL94 V0 and 5VA listing.
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP WFP36 PBT (Europe-Africa-Middle East) LNP* Lubricomp* WFP36 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Silicone.
Flexural Yield Strength	135 MPa	19600 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Lubricomp ZFL34 PPO LNP* Lubricomp* ZFL34 is a compound based on Modified PPO containing glass fiber and PTFE.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem DT1800E PEI Blend Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Americas re..
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem DT1800E PEI Blend (Asia Pacific) Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacifi..
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem DT1800E PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Afri..
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem DT1810E PEI Blend Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Americas re..
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem DT1810E PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacifi..
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem DT1810E PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Afri..
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM DT1810EV PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed.
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem DT1810EV PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed.This data was supplied by SABIC-IP for..
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM EXUM0169 PEI Blend Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM EXUM0169 PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem EXUM0169 PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Afri..
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP 2X98703 ETFE LNP* THERMOCOMP* 2X98703 is a compound based on ETFE Copolymer resin containint Proprietary Filler(s).
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Noryl GTX GTX8110 PPE+PA (Europe-Africa-Middle East) GTX8110 is a glass filled extrudable Noryl GTX with low thermal conductivity, suitable for thermal breaksThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Yield Strength	135 MPa	19600 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL IGN5531 PPE+PS Noryl* IGN5531 is an 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Nor..
Flexural Yield Strength	135 MPa	19600 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL IGN5531 PPE+PS (Asia Pacific) Noryl* IGN5531 is an 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Nor..
Flexural Yield Strength	135 MPa	19600 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL IGN5531 PPE+PS (Europe-Africa-Middle East) Noryl* IGN5531 is an 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Nor..
Flexural Yield Strength	135 MPa	19600 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 9076 PEI (Europe-Africa-Middle East) Standard flow Polyetherimide Blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution.
Flexural Yield Strength	135 MPa	19600 psi
3M Z100™ Restorative Dental Composite 3M™ Z100™ restorative is an all purpose, esthetic, light cured dental composite. 3M Restorative Z100 features a translucency and opalescence similar to that of natural teeth and is used for porce..
Flexural Yield Strength	135 MPa	19600 psi	DIN 53 452
Albis Plastics Tedur® P 9529 PPS, ~55% Glass Fiber/Mineral (black only) Compounded Regrind and/or Production Scrap, Excellent Cost-Performance Ratio. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Lamp Holders, Lamp SocketsProcessing: Inj..
Flexural Yield Strength	135 MPa	19600 psi	ASTM Data
BASF Capron® 5202CQ Blend HS Blend Nylon 66 (Dry) (discontinued **) Capron 5202CQ HS Blend is a heat stabilized, blended polyamide 6,6 injection molding homopolymer developed for fast molding cycles. It is also available in pigmented versions.Capron 5202CQ HS Blend..