Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 56.0 MPa | 8120 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics GELOY CR3020 ASA Low-gloss ASA for profile and capstock applications |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Geloy XTWE265 ASA Highly weatherable Geloy ASA profile extrusion grade for processes with simple or no calibration hardware.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics GELOY XTWE265 ASA (Asia Pacific) Highly weatherable Geloy ASA profile extrusion grade for processes with simple or no calibration hardware. |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Geloy XTWE265 ASA (Europe-Africa-Middle East) Highly weatherable Geloy ASA profile extrusion grade for processes with simple or no calibration hardware.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Geloy XTWE270M ASA+SAN (Asia Pacific) Excellent weatherability, good flow/aesthetics and good impact.Profile co-extrusion grade over ABS, PVC or other compatible polymers. XTWE270M is available in various colours.This data was supplied.. |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Geloy XTWE270M ASA+SAN (Asia Pacific) Excellent weatherability, good flow/aesthetics and good impact.Profile co-extrusion grade over ABS, PVC or other compatible polymers. XTWE270M is available in various colours.This data was supplied.. |
|||
Flexural Yield Strength | 56.0 - 159 MPa | 8120 - 23000 psi | Average value: 88.2 MPa Grade Count:49 |
Overview of materials for Polyphenylene Ether, Heat Resistant This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Heat Resistant". Each property range of values reported is minimum and maximum valu.. |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | ASTM D790 |
North Wood Plastics Polypropylene with 20% Wood Fiber, Extrusion Grade Data provided by North Wood Plastics, Inc. |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | ASTM D790 |
North Wood Plastics PS with 40% Wood Fiber Data provided by North Wood Plastics, Inc. |
|||
Flexural Yield Strength | 56.0 - 115 MPa | 8120 - 16700 psi | Average value: 87.0 MPa Grade Count:3 |
Overview of materials for Phenolic/Rubber; Molded This property data is a summary of similar materials in the MatWeb database for the category "Phenolic/Rubber; Molded". Each property range of values reported is minimum and maximum values of approp.. |
|||
Flexural Yield Strength | 56.0 - 275 MPa | 8120 - 39900 psi | Average value: 205 MPa Grade Count:24 |
Overview of materials for Nylon 66/6, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are incl.. |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | ASTM D790 |
Hannam Chemical Hanalac 711 ABS, Plating Grade Plating grade with excellent moldability and easy to surface treat. It also has a strong adhesive strength after plating and an excellent heat cycle. Applications: Appliances, TV frames, automoti.. |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 337 PBT Low temperature impact PBT. Automotive applications: underhood power distribution boxes and covers. |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-LOY A3000LTH ABS LNP* STAT-LOY* A3000LTH is a compound based on ABS resin. Added features of this material include: Transparent, Antistatic, Formulation Locked. |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP WH0270F PBT LNP* Thermocomp* WH0270F is a dense compound based on PBT. |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP PB006EQ PA 6 (Europe-Africa-Middle East) LNP *THERMOCOMP* PB006EQ is a compound based on PA 6 containing Glass Bead. Added features include Reduced Moisture. |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp WH0270FX_WH5A289 PBT 2.7 specific gravity PBTThis data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermotuf PX06093 PA 6 (Europe-Africa-Middle East) LNP* THERMOTUF* PX06093 is a compound based on PA 6 resin containing Impact Modifier. Added features include: High Impact, UV-Stabilized, Laser Marking Grade.This data was supplied by SABIC-IP for t.. |
|||
Flexural Yield Strength | 56.0 MPa | 8120 psi | 2 mm/min; ISO 178 |
Eurostar Staramide PX06093 PA6, Impact Modified, Injection Molded Staramide PX06093 is an UV Stabilized, Impact Modified Polyamide 6 Injection Molding Resin (also known as P1000HI020UVL)Information provided by Eurostar. |
|||
Flexural Yield Strength | 56.0 - 82.0 MPa | 8120 - 11900 psi | Average value: 68.8 MPa Grade Count:19 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Plating Grade This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Plating Grade". Each property range of values reported is minimum.. |