SABIC Innovative Plastics Valox® 337 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 337 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low temperature impact PBT. Automotive applications: underhood power distribution boxes and covers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Viscosity | 1.20e+6 cP | 1.20e+6 cP | Melt Viscosity; SABIC Method |
| Linear Mold Shrinkage, Flow | 0.024 - 0.027 cm/cm @Thickness 3.20 mm |
0.024 - 0.027 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.024 - 0.027 cm/cm @Thickness 3.20 mm |
0.024 - 0.027 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 12.7 g/10 min @Load 5.00 kg, Temperature 250 °C |
12.7 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 3.9 % | 3.9 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 56.0 MPa | 8120 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.79 GPa | 260 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 8.70 J/cm | 16.3 ft-lb/in | ASTM D256 |
| 8.01 J/cm @Temperature -30.0 °C |
15.0 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 32.04 J/cm | 60.02 ft-lb/in | ASTM D4812 |
| 32.04 J/cm @Temperature -30.0 °C |
60.02 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C @Thickness 6.40 mm |
208 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C @Thickness 6.40 mm |
117 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® HD-2007-H HDPE Extrusion Resin
- Hong Kun Group Canthaxanthin Feed Additive
- Kennametal Stellite Stellite® 2012 Cobalt Alloy
- LG Chemical Lupox® SG5152 PBT+PET+GF15%
- Minelco MagnaDense 14 Coarse Aggregate
- Sekisui PIOCELAN OP-15D Moldable Polymer Foam
- SABIC Innovative Plastics LNP THERMOCOMP PF00DS PA 6 (Europe-Africa-Middle East)
- Dow Corning SILASTIC® Q4-2857 SILICONE RUBBER
- Dow Engage® ENX 7458.00 Ethylene-Butene Copolymer
- BASF Ultramid® A3UG5 BK 23260 25% Glass Filled PA66 (Dry)
Copyright © lookpolymers.com All Rights Reserved