- Polymer Property : Flexural Yield Strength = 127 MPa
Polymer Property : Flexural Yield Strength = 127 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 127 MPa | 18400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DFP36 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFP36 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Silicone. |
|||
| Flexural Yield Strength | 127 MPa | 18400 psi | 6.4 mm; ASTM D790 |
| SABIC Innovative Plastics Lexan® FL930 PC Various weight reductions at 0.250"" (6.35 mm) wall, 30% GR. Superior flex strength/modulus, good tensile strength. V-0/5VA at 0.250"" (6.35 mm). |
|||
| Flexural Yield Strength | 127 MPa | 18400 psi | 6.4 mm; ASTM D790 |
| SABIC Innovative Plastics Lexan® FL930 PC (Asia Pacific) Various weight reductions at 0.250"" (6.35 mm) wall, 30% GR. Superior flex strength/modulus, good tensile strength. V-0/5VA at 0.250"" (6.35 mm). |
|||
| Flexural Yield Strength | 127 MPa | 18400 psi | 6.4 mm; ASTM D790 |
| SABIC Innovative Plastics Lexan® FL933 PC Various weight reductions at 0.250"" wall. 30% GR. Superior flexural strength and modulus; good tensile strength. UV-stabilized. |
|||
| Flexural Yield Strength | 127 MPa @Thickness 3.20 mm |
18500 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUCEL GC210 POM+GF10%, High Rigidity Feature: Injection Molding, POM+GF10%, High RigidityApplication: Casings of Pump and Pivot BearingsCAS No. 66455-31-0 and 65997-17-3Information provided by LG Chemical |
|||
| Flexural Yield Strength | 127 MPa @Thickness 6.40 mm |
18500 psi @Thickness 0.252 in |
1mm/min; ASTM D790 |
| LG Chemical LUCON PN9008 PPS+MF+GF Injection Molding Grade, PPS+MF+GF, High Thermal Conductivity, Chemical Resistance, High Heat ResistanceApplication: Electrical or Electronic Parts (Heat sink, LED etc.), Motor HousingsCAS No. 25212.. |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN126 General Purpose Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Flexural Yield Strength | 127 MPa @Thickness 3.20 mm |
18500 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUMAX HR5157 PBT+ABS+GF15%, Heat Resistance Description: Injection Molding Grade, PBT+ABS+GF15%, Heat ResistanceApplication: E&E (CD ROM Tray)CAS: 9003-56-9, 65997-17-3, 24968-12-5 and 25038-59-9Information provided by LG Chemical |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN136 General Purpose Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Flexural Yield Strength | 127 MPa @Thickness 3.20 mm |
18500 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUMID GP3300B(W) PA66+MF30%, General Purpose Feature: Injection Molding, PA66+MF30%, General PurposeApplication: Automotive (Engine Cover))CAS No. 25038-54-4 and 9010-79-1Information provided by LG Chemical |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN3311 General Purpose Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin.. |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN171 General Purpose Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN178MT40 M/F Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN3311N General Purpose Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin.. |
|||
| Flexural Yield Strength | 127 MPa @Thickness 6.40 mm |
18500 psi @Thickness 0.252 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUPOL LW4405 PP+GF/MF40% Description: Injection Molding, PP+GF/MF40%, Low WarpageApplication: Electrical, Electronic and Automotive Parts CAS: 9003-07-0, 65997-17-3 and 12001-26-2Information provided by LG Chemical |
|||
| Flexural Yield Strength | 127 MPa @Thickness 3.20 mm |
18500 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOS GP2200 ABS+GF20%, General Purpose Feature: Injection Molding, ABS+GF20%, General PurposeApplication: Electric & Electronic (Housing, Components)CAS No. 9003-56-9, 9003-54-7 and 65997-17-3Information provided by LG Chemical |
|||
| Flexural Yield Strength | 127 MPa | 18400 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON Noryl_HMC3008A PPE+PS LNP* Stat-kon* Noryl_HMC3008A compound is a 30% glass/mineral/carbon fiber reinforced resin; static dissipative; 250F (120C) HDT. Tight tolerance molding. |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | ASTM D790 |
| Samyang Tribit® 1550GN15 PBT Alloy, Reinforced Flame Retardancy Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1550GN15 is a reinforced, flame retardant (.. |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | ASTM D790 |
| Samyang Trirex® 3025G10 Polycarbonate, 10% Glass Reinforced TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, elec.. |
|||
| Flexural Yield Strength | 127 MPa | 18400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL NH7111E PPE+HIPS (Asia Pacific) Noryl* EXNL0280 is a glass fiber reinforced, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and low warpage, this resin also uses non-halogenated FR a.. |
|||
| Flexural Yield Strength | 127 MPa | 18400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP 9X02841 PBT+PC LNP* Thermocmop* 9X02841 is a PBT/Polycarbonate blend containing proprietary fillers. |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | ASTM D790 |
| Cheng Yu Plastic N66C3 Nylon 66, 30% Mineral Reinforced |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | ASTM D790 |
| Cheng Yu Plastic N6C2 Nylon 6, 20% Mineral Reinforced |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | ASTM D790 |
| Cheng Yu Plastic T882GV1 Flame Retardant PBT, 10% Glass Fiber |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | ASTM D790 |
| Cheng Yu Plastic T888G1 PBT, 10% Glass Fiber |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | ASTM D790 |
| Cheng Yu Plastic A703G2 ABS 20% Glass Fiber Reinforced |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | ASTM D790 |
| Cheng Yu Plastic FRCV150 Flame Retardant Nylon 66, 20% Mineral Reinforced |
|||
| Flexural Yield Strength | 127 MPa | 18400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL44 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL44 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. |
|||
| Flexural Yield Strength | 127 MPa @Thickness 3.20 mm |
18500 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUPOY GP2100 PC+GF10%, Heat Resistance Description: Injection Molding, PC+GF10%, General Purpose, Heat ResistanceApplication: IT/OA, E&E Housing and Components, Automotive (Interior)CAS: 103598-77-2 and 65997-17-3Information provided by .. |
|||
| Flexural Yield Strength | 127 MPa | 18500 psi | ASTM D790 |
| Cheng Yu Plastic ML3410 PC, 10% Glass Fiber |
|||