Polymer Property : Flexural Yield Strength = 103 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	103 MPa	14900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® 500R PC (Asia Pacific) 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. Internal mold release.
Flexural Yield Strength	103 MPa	14900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® 503 PC (Asia Pacific) 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. UV-stabilized.
Flexural Yield Strength	103 MPa	14900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® 503R PC 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. UV-stabilized. Internal mold release.
Flexural Yield Strength	103 MPa	14900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® CFR5630D PC COPOLYMER (Asia Pacific) LEXAN™ CFR5630D Polycarbonate (PC) is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC resin meets FAR25.853 smoke density a..
Flexural Yield Strength	103 MPa	14900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® CFR7630 PC COPOLYMER (Europe-Africa-Middle East) Lexan* CFR7630 Polycarbonate (PC) resin is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm ..
Flexural Yield Strength	103 MPa	14900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® CFR9111 PC COPOLYMER Lexan* CFR9111 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm and good flow capability. ..
Flexural Yield Strength	103 MPa	14900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® LUX7636C PC COPOLYMER (Europe-Africa-Middle East) Lexan* LUX7636C Polycarbonate (PC) resin is a non-filled, extrudable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm / 5VA rating at 3.0mm and is U..
Flexural Yield Strength	103 MPa	14900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® LUX9130C PC COPOLYMER Lexan* LUX9130C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and..
Flexural Yield Strength	103 MPa	14900 psi	ASTM D790
PolyOne Geon™ CPVC MC500 Polyvinyl Chloride, Chlorinated (CPVC) The Geon MC500 CPVC is an injection molding fittings compound for Industrial Pipe applications where enhanced resistance at elevated temperatures is needed. Geon MC500 demonstrates superior processa..
Flexural Yield Strength	103 MPa	14900 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics Cycoloy® C6200 PC+ABS Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs.
Flexural Yield Strength	103 MPa	14900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Cycoloy® CX7211 PC+ABS (Europe-Africa-Middle East) Cycoloy* CX7211 PC/ABS resin is a non-filled, injection moldable grade which has UL 94 rating at 2.5 mm 5VA. Cycoloy CX7211 resin provides all color options and features an excellent balance of flo..
Flexural Yield Strength	103 MPa	14900 psi	ASTM D790
Ineos Nova 1280 High Heat Crystal Polystyrene (discontinued **) Good processing characteristics, Low residual monomer, Low oligomersApplications: Direct injection foam, Biaxially oriented sheet, Glazing sheetExposure to gamma radiation in the 2.02-6.06 megarad r..
Flexural Yield Strength	103 MPa	14900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® CFR9131 PC COPOLYMER (Asia Pacific) Lexan* CFR9131 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and ..
Flexural Yield Strength	103 MPa	14900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® LUX9130C PC COPOLYMER (Asia Pacific) Lexan* LUX9130C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and..
Flexural Yield Strength	103 MPa	14900 psi	ASTM D790
Firestone CL200-001 Nylon 6 Natural color. Not heat stabilized or modified. Lubricated. Chip size is 2 x 3.5 mm.Information provided by Firestone
Flexural Yield Strength	103 MPa @Thickness 3.20 mm	14900 psi @Thickness 0.126 in	10mm/min; ASTM D790
LG Chemical LUPOY GP1006FL PC, Flame Retardant Description: Injection Molding, PC, Flame Retardant, High FlowApplication: IT/OA, E&E Housing and ComponentsCAS: 103598-77-2Information provided by LG Chemical
Flexural Yield Strength	103 MPa	14900 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC1010 PPE+HIPS (Europe-Africa-Middle East) LNP* Stat-kon* HMC1010 compound is a 10% Carbon fiber reinforced. Static dissipative. Nonbrominated, nonchlornated flame retardant system. UL94 V-1 rated.
Flexural Yield Strength	103 MPa	15000 psi	ASTM D790
Techmer ES PlastiblendÂ® PC/ABS 88 GF 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 10% Filler by WeightInformation provided by TP Composites, Inc.
Flexural Yield Strength	103 MPa	14900 psi	ASTM D790
Sumitomo Bakelite North America RXÂ® 2-501N Mineral Filled Diallyl Phthalate Isophthalate DAP Resin Isomer. Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Conforms with the requirements of ASTM D5948..
Flexural Yield Strength	103 MPa	14900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL NH5120C PPE+PS (Asia Pacific) Noryl* NH5120C resin is a modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, good chemical resistance, and low specifc gravity for light weight parts. The ..
Flexural Yield Strength	103 MPa	14900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL EXNL0357 PPE+PS
Flexural Yield Strength	103 MPa	14900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GTX GTX674PC PPE+PA6 A conductive PPE/PA blend designed to have improved surface appearance and elevated heat resistance for powder coating. The material is suitable for injection molding. The material is only availab..
Flexural Yield Strength	103 MPa	15000 psi	ASTM D790
PlastxWorld CEVIAN®-N 055 SAN resin These are typical values and are not intended for specification purposes. UL approved file No. is E142893. Information provided by PlastxWorld Inc.
Flexural Yield Strength	103 MPa	15000 psi	ASTM D790
Westlake Plastics Zelux® 10% GF Polycarbonate 10% Glass Filled Zelux polycarbonate is a transparent engineering plastic with excellent dimensional stability and good mechanical and electrical properties. It is used for structural applications when clarity and ..
Flexural Yield Strength	103 MPa	15000 psi	ASTM D790
Clariant Renol PC010-L FR Polycarbonate, Glass Reinforced, Flame Retardant Data provided by Clariant Masterbatches
Flexural Yield Strength	103 MPa	14900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® LUX7636C PC COPOLYMER (Asia Pacific) Lexan* LUX7636C Polycarbonate (PC) resin is a non-filled, extrudable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm / 5VA rating at 3.0mm and is U..
Flexural Yield Strength	103 MPa	14900 psi	ASTM D790
Sumitomo Bakelite North America FS-6 CAF Mineral Filled Diallyl Phthalate Isophthalate DAP Resin Isomer. Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type MI..
Flexural Yield Strength	103 MPa	14900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® LUX7630C PC COPOLYMER (Asia Pacific) Lexan* LUX7630C Polycarbonate (PC) resin is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm..
Flexural Yield Strength	103 MPa	14900 psi	ASTM D790
PlastxWorld CEVIAN® B5522 10% GF PBT/ABS Alloy Glass fiber reinforced and flame retarded PBT/ABS alloy.Information provided by PlastxWorld Inc.
Flexural Yield Strength	103 MPa	14900 psi	ASTM D790
Ineos Nova 1204 High Heat Crystal Polystyrene Good processing characteristics, High tensile strength and modulus, Excellent clarity, USP Class VIApplications: Direct injection foam, Biaxially oriented sheet, Glazing sheetExposure to gamma radia..