Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Modulus | 81.4 GPa | 11800 ksi | |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 10% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
Shear Modulus | 81.4 GPa | 11800 ksi | |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 15% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
Shear Modulus | 81.4 GPa | 11800 ksi | |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 20% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
Shear Modulus | 81.4 GPa | 11800 ksi | |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 30% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of .. |
|||
Shear Modulus | 81.4 GPa | 11800 ksi | |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 40% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of .. |
|||
Shear Modulus | 81.4 GPa | 11800 ksi | |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 5% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
Shear Modulus | 81.4 GPa | 11800 ksi | |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 50% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of .. |
|||
Shear Modulus | 81.4 GPa | 11800 ksi | |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950°F (1070°C)/5 minutes/AC. This produces ASTM grain size 9.5. Other property values are ty.. |
|||
Shear Modulus | 81.4 GPa | 11800 ksi | |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1400°F (760°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950°F (1070°C)/5 minutes/AC + Aged 1400°F (760°C)/100h/AC. This produces ASTM grain siz.. |
|||
Shear Modulus | 81.4 GPa | 11800 ksi | |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC. This produces ASTM grain size 5.5. Other property values are ty.. |
|||
Shear Modulus | 81.4 GPa | 11800 ksi | |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) + Aged 1200°F (650°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC + Aged 1200°F (650°C)/100h/AC. This produces ASTM grain siz.. |
|||
Shear Modulus | 81.4 GPa | 11800 ksi | |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) + Aged 1400°F (760°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC + Aged 1400°F (760°C)/100h/AC. This produces ASTM grain siz.. |
|||
Shear Modulus | 81.4 GPa | 11800 ksi | |
Carlson C 601 Nickel-Chromium-Iron Alloy General DescriptionCarlson Alloy C 6021 is a nickel-chromium alloy, developed specifically for high –temperature service. This alloy exhibits outstanding resistance to both cyclic and static oxida.. |
|||
Shear Modulus | 81.4 GPa | 11800 ksi | |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1200°F (650°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950°F (1070°C)/5 minutes/AC + Aged 1200°F (650°C)/100h/AC. This produces ASTM grain size 9.5. .. |