Polymer Property : Shear Modulus = 11000 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Modulus	76.0 GPa	11000 ksi
Special Metals DURANICKELÂ® 301 (UNS N03301) Annealed and Aged Rod and Bar Tensile strength (ultimate and yield), compressive strength, hardness, and elongation values reported here are typical for Annealed and Aged Rod and Bar specifically. Other property values are typic..
Shear Modulus	76.0 GPa	11000 ksi
Special Metals DURANICKELÂ® 301 (UNS N03301) Annealed and Aged Wire Tensile strength (ultimate) and elongation values reported here are typical for Annealed and Aged Wire specifically. Other property values are typical of aged DURANICKELÂ® alloy 301 or the alloy i..
Shear Modulus	76.0 GPa	11000 ksi
Special Metals DURANICKELÂ® 301 (UNS N03301) Annealed Rod and Bar Tensile strength (ultimate and yield), compressive strength, hardness, and elongation values reported here are typical for Annealed Rod and Bar specifically. Other property values are typical of ann..
Shear Modulus	76.0 GPa	11000 ksi
Special Metals DURANICKELÂ® 301 (UNS N03301) Annealed Strip Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Annealed Strip specifically. Other property values are typical of annealed DURANICKELÂ® alloy 3..
Shear Modulus	76.0 GPa	11000 ksi
Special Metals DURANICKELÂ® 301 (UNS N03301) Annealed Wire Tensile strength (ultimate) and elongation values reported here are typical for Annealed Wire specifically. Other property values are typical of annealed DURANICKELÂ® alloy 301 or the alloy in gen..
Shear Modulus	76.0 GPa	11000 ksi
Special Metals DURANICKELÂ® 301 (UNS N03301) Cold-Drawn Rod and Bar Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Cold-Drawn Rod and Bar specifically. Other property values are typical of annealed DURANICKELÂ®..
Shear Modulus	76.0 GPa	11000 ksi
Special Metals DURANICKELÂ® 301 (UNS N03301) Half-Hard and Aged Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Half-Hard and Aged Strip specifically. Other property values are typical of aged DURANICKELÂ® alloy 301 o..
Shear Modulus	76.0 GPa	11000 ksi
Special Metals DURANICKELÂ® 301 (UNS N03301) Half-Hard Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Half-Hard Strip specifically. Other property values are typical of annealed DURANICKELÂ® alloy 301 or the..
Shear Modulus	76.0 GPa	11000 ksi
Special Metals DURANICKELÂ® 301 (UNS N03301) Hot-Finished and Aged Rod and Bar Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Hot-Finished and Aged Rod and Bar specifically. Other property values are typical of aged DURANIC..
Shear Modulus	76.0 GPa	11000 ksi
Special Metals DURANICKELÂ® 301 (UNS N03301) Hot-Finished Rod and Bar Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Hot-Finished Rod and Bar specifically. Other property values are typical of annealed DURANICKELÂ..
Shear Modulus	76.0 GPa	11000 ksi
Special Metals DURANICKELÂ® 301 (UNS N03301) Spring Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Spring Strip specifically. Other property values are typical of annealed DURANICKELÂ® alloy 301 or the al..
Shear Modulus	76.0 GPa	11000 ksi
Special Metals DURANICKELÂ® 301 (UNS N03301) Spring Wire Tensile strength (ultimate) and elongation values reported here are typical for Spring Wire specifically. Other property values are typical of annealed DURANICKELÂ® alloy 301 or the alloy in gener..
Shear Modulus	76.0 GPa	11000 ksi
Special Metals DURANICKELÂ® 301 (UNS N03301) Spring Wire, Aged Tensile strength (ultimate) and elongation values reported here are typical for Spring Wire, Aged specifically. Other property values are typical of aged DURANICKELÂ® alloy 301 or the alloy in gen..
Shear Modulus	76.0 GPa	11000 ksi	Dynamic Method
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 3 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness Tensile strength (ultimate and yield), shear strength, and elongation values reported here are typical for Cold Rolled Sheet, 3 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness samples. Density a..
Shear Modulus	76.0 GPa	11000 ksi	Dynamic Method
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 3 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness Tensile and bearing strengths (ultimate and yield) and elongation values reported here are typical for Cold Rolled Sheet, 3 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness samples. Density and m..
Shear Modulus	76.0 GPa	11000 ksi	Precipitation Hardened, Dynamic Method
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, Solution Treated Tensile strength (ultimate and yield), and elongation values reported here are typical for Cold Rolled Sheet, Solution Treated samples. Density and magnetic permeability are typical of annealed INCO..
Shear Modulus	76.0 GPa	11000 ksi	Dynamic Method
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Forged Disc, 2 Part Heat Treatment Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, 2 Part Heat Treatment samples. Density and magnetic permeability are typica..
Shear Modulus	76.0 GPa	11000 ksi	Dynamic Method
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Forged Disc, 3 Part Heat Treatment Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, 3 Part Heat Treatment samples. Density and magnetic permeability are typica..
Shear Modulus	76.0 GPa	11000 ksi	Precipitation Hardened, Dynamic Method
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Forged Disc, Solution Treated Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, Solution Treated samples. Density and magnetic permeability are typical of ..
Shear Modulus	76.0 GPa	11000 ksi	Dynamic Method
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter Tensile strength (ultimate and yield), shear strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 3 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter s..
Shear Modulus	76.0 GPa	11000 ksi	Dynamic Method
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diameter Tensile strength (ultimate and yield), compressive strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diamete..
Shear Modulus	76.0 GPa	11000 ksi	Calculated
Sapco Partially Stabilized TZP Zirconia (YSZ) Information provided by Sapco.
Shear Modulus	76.0 GPa	11000 ksi
Elgiloy® Co-Cr-Ni Alloy, Wire, 10% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f..
Shear Modulus	75.8 GPa	11000 ksi
Crucible Steel 20 Cb Plus Stainless Steel Crucible 20 Cb Plus is a non-hardenable stabilized stainless steel with exceptional resistance to sulfuric, phosphoric, and nitric acid. This grade also has good resistance to stress corrosion crack..
Shear Modulus	75.8 GPa	11000 ksi
Crucible Steel 410 Chromium Steel Crucible 410 is a hardenable chromium steel which is adaptable for general purpose corrosion resisting and heat resisting applications. This grade is magnetic at times. Information provided by Cruci..
Shear Modulus	75.8 GPa	11000 ksi
Carlson C 600 Nickel-Chromium-Iron Alloy Carlson Alloy C 600 is nickel-chromium alloy, developed for use in severely corrosive environments at elevated temperatures. The high nickel content of this alloy provides excellent resistance to c..
Shear Modulus	75.8 GPa	11000 ksi
Carlson C 600ESR Nickel-Chromium-Iron Alloy General DescriptionCarlson Alloy C 600 is nickel-chromium alloy, developed for use in severely corrosive environments at elevated temperatures. The high nickel content of this alloy provides excell..
Shear Modulus	75.8 GPa @Temperature 232 °C	11000 ksi @Temperature 450 °F	Annealed
Latrobe MP159® Alloy MP159 is an alloy of the Multiphase family of alloys possessing the unique combination of ultra-high strength, ductility and corrosion resistance. Through work strengthening and aging, MP159 alloy ..
Shear Modulus	76.0 GPa	11000 ksi	Dynamic Method
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 2 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness Tensile and bearing strengths (ultimate and yield) and elongation values reported here are typical for Cold Rolled Sheet, 2 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness samples. Density and m..
Shear Modulus	76.0 GPa	11000 ksi	Dynamic Method
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 2 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter Tensile strength (ultimate and yield), shear strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 2 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter s..