Special Metals DURANICKEL® 301 (UNS N03301) Hot-Finished Rod and Bar
| Category | Metal , Nonferrous Metal , Nickel Alloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | DURANICKEL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals DURANICKEL® 301 (UNS N03301) Hot-Finished Rod and Bar.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Hot-Finished Rod and Bar specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the alloy in general.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.19 g/cc | 0.296 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 140 - 240 | 140 - 240 | 3000 kg |
| Hardness, Rockwell B | >= 75 | >= 75 | |
| Hardness, Rockwell C | <= 22 | <= 22 | |
| Tensile Strength, Ultimate | 621 - 896 MPa | 90000 - 130000 psi | |
| Tensile Strength, Yield | 241 - 621 MPa @Strain 0.200 % |
35000 - 90000 psi @Strain 0.200 % |
|
| Elongation at Break | 30 - 55 % | 30 - 55 % | |
| Modulus of Elasticity | 207 GPa | 30000 ksi | Tension |
| Poissons Ratio | 0.31 | 0.31 | |
| Fatigue Strength | 295 MPa @# of Cycles 1.00e+8 |
42800 psi @# of Cycles 1.00e+8 |
rotating beam |
| Shear Modulus | 76.0 GPa | 11000 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean; aged |
| 14.0 µm/m-°C @Temperature 21.0 - 300 °C |
7.78 µin/in-°F @Temperature 69.8 - 572 °F |
Mean; aged | |
| 14.7 µm/m-°C @Temperature 21.0 - 500 °C |
8.17 µin/in-°F @Temperature 69.8 - 932 °F |
Mean; aged | |
| 16.6 µm/m-°C @Temperature 21.0 - 900 °C |
9.22 µin/in-°F @Temperature 69.8 - 1650 °F |
Mean; aged | |
| Specific Heat Capacity | 0.435 J/g-°C @Temperature 20.0 - 100 °C |
0.104 BTU/lb-°F @Temperature 68.0 - 212 °F |
|
| Thermal Conductivity | 23.8 W/m-K | 165 BTU-in/hr-ft²-°F | Age Hardened |
| Melting Point | 1400 - 1440 °C | 2550 - 2620 °F | |
| Solidus | 1400 °C | 2550 °F | |
| Liquidus | 1440 °C | 2620 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 4.0 - 4.75 % | 4.0 - 4.75 % | |
| Carbon, C | <= 0.30 % | <= 0.30 % | |
| Copper, Cu | <= 0.25 % | <= 0.25 % | |
| Iron, Fe | <= 0.60 % | <= 0.60 % | |
| Manganese, Mn | <= 0.50 % | <= 0.50 % | |
| Nickel, Ni | >= 93 % | >= 93 % | Including Cobalt |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.010 % | <= 0.010 % | |
| Titanium, Ti | 0.25 - 1.0 % | 0.25 - 1.0 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000424 ohm-cm | 0.0000424 ohm-cm | Aged |
| Curie Temperature | 15.0 - 50.0 °C | 59.0 - 122 °F |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WR7426L Polyvinyl Chloride, Flexible (PVC, Flexible)
- Old Hickory M&M Clays, Inc. Wilco-LPC Kaolin Clay
- Total Lacqtene® 2006 TN 35 HDPE pipe coating (discontinued **)
- KB Alloys Ticar® 5% Ti - 0.18% C Titanium Carbon Aluminum Rod
- Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours
- LG Chemical LUPOY GN5101RF PC/ABS Mineral Filler
- Lucite International Elvacite ® 2041 Acrylic Resin
- Vyncolit Neopreg Kinel® SK4503 S5 Aramid Reinforced Molding Compound
- LNP Lubricomp® JFL-4036 Polyethersulfone, Glass Fiber Reinforcement, PTFE Lubricant (discontinued **)
- Polymer Resources PPX/NY G30 Modified PPO, 30% Glass Reinforced PPX/Nylon 6,6 Alloy (Unverified Data**)&l
Copyright © lookpolymers.com All Rights Reserved