Special Metals DURANICKEL® 301 (UNS N03301) Spring Wire, Aged
| Category | Metal , Nonferrous Metal , Nickel Alloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | DURANICKEL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals DURANICKEL® 301 (UNS N03301) Spring Wire, Aged.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tensile strength (ultimate) and elongation values reported here are typical for Spring Wire, Aged specifically. Other property values are typical of aged DURANICKEL® alloy 301 or the alloy in general.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.19 g/cc | 0.296 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 1380 - 1650 MPa | 200000 - 240000 psi | |
| Elongation at Break | 5.0 - 10 % | 5.0 - 10 % | |
| Modulus of Elasticity | 207 GPa | 30000 ksi | Tension |
| Poissons Ratio | 0.31 | 0.31 | |
| Shear Modulus | 76.0 GPa | 11000 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| 14.0 µm/m-°C @Temperature 21.0 - 300 °C |
7.78 µin/in-°F @Temperature 69.8 - 572 °F |
Mean | |
| 14.7 µm/m-°C @Temperature 21.0 - 500 °C |
8.17 µin/in-°F @Temperature 69.8 - 932 °F |
Mean | |
| 16.6 µm/m-°C @Temperature 21.0 - 900 °C |
9.22 µin/in-°F @Temperature 69.8 - 1650 °F |
Mean | |
| Thermal Conductivity | 23.8 W/m-K | 165 BTU-in/hr-ft²-°F | |
| Melting Point | 1400 - 1440 °C | 2550 - 2620 °F | |
| Solidus | 1400 °C | 2550 °F | |
| Liquidus | 1440 °C | 2620 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 4.0 - 4.75 % | 4.0 - 4.75 % | |
| Carbon, C | <= 0.30 % | <= 0.30 % | |
| Copper, Cu | <= 0.25 % | <= 0.25 % | |
| Iron, Fe | <= 0.60 % | <= 0.60 % | |
| Manganese, Mn | <= 0.50 % | <= 0.50 % | |
| Nickel, Ni | >= 93 % | >= 93 % | Including Cobalt |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.010 % | <= 0.010 % | |
| Titanium, Ti | 0.25 - 1.0 % | 0.25 - 1.0 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000424 ohm-cm | 0.0000424 ohm-cm | |
| Curie Temperature | <= 95.0 °C | <= 203 °F |
Users viewing this material also viewed the following:
- MV Labs MN400 MnCl2·4H2O Manganese(II) chloride tetrahydrate
- Karina E 72/206-IS Crystal PVC Compound (SP32811)
- SABIC Innovative Plastics ULTEM ATX100 PEI+PCE
- SABIC Innovative Plastics Noryl EN110 PPE+PS (Asia Pacific)
- Lubrizol Telene 1620 A/BK Dicyclopentadiene (DCPD)
- Zeon Chemicals Zeonex® E48R Cyclo-Olefin Polymer
- Denka TE-30 Transparent Resin Polymer (MABS resin) ABS
- Akzo Nobel Trigonox® EHP-W60 Polymerization Initiator
Copyright © lookpolymers.com All Rights Reserved