Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 60.0 - 70.0 MPa | 8700 - 10200 psi | Type 1B, 50mm/min; ISO 527-1/2:1993 |
Nylacast Cast Nylon 6, Glass Filled Information provided by Nylacast Ltd. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
Nylene® PA6/6 Impact Modified 311 HS Nylon 6/6 Medium Impact Grade; Property data for dry as molded samples.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® XCM850 PC+ABS Reinforced PC/ABS with high stiffness and low CTE. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® 505R PC (Asia Pacific) Lexan* 505R Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. Lexan 505R contains non-chlorinated, non-brominated flame retardant systems with UL-94 V0 rating at 1.5mm... |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FXM3729 PC (Europe-Africa-Middle East) LEXAN FXM3729 is an UV stabilized Visual FX Sparkle grade, with an excellent flow. It contains a release agent to ensure easy processing.This data was supplied by SABIC-IP for the Europe-Africa-Midd.. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | 5.1 mm/min; ASTM D638 |
PolyOne Edgetek® X TR2-10GF/000 NATURAL Copolyester The Edgetek™ engineering thermoplastics compounds made with Eastman Tritan™ copolyester offer a wide range of performance and properties with the addition of reinforcing additives. By utilizing Ea.. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® 143X PC Copolymer (Asia Pacific) Improved flow PC with excellent processability and mold release. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50mm/min; ASTM D638 |
LG Chemical Lupoy 1201-05 Polycarbonate Resin Description: LUPOY PC 1201-05 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 |
Mitsubishi Xantar® 24 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 |
Mitsubishi Xantar® MX 2021 Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50mm/min; ASTM D638 |
LG Chemical Lupoy 1300-12 Polycarbonate Resin Description: LUPOY PC 1300-12 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527 type 1 A |
Solvay TECHNYL® A 402 Natural FA PA66, Conditioned Description: Unreinforced polyamide PA66, very high viscosity, for extrusion.Available in: Europe and North AmericaProduct Applications: TECHNYL® A 402 NATURAL FA offers three main advantages: hi.. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527 type 1 A |
Solvay TECHNYL® A 402H1 Natural PA66, Conditioned Description: TECHNYL® A 402H1 is an unreinforced polyamide 66, very high viscosity, heat stabilized, for extrusion and injection molding. This product is available in natural color.Benefits: The .. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
Solvay TECHNYL® eXten D247 F Nylon 66 & 610 Description: Polyamid 66 & 610, impact modified, alkali resistance, mold release, for injection molding. This material is available in natural color and in colors on requestAvailable in: Asia Pacifi.. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics XYLEX X8419 PC+POLYESTER (Asia Pacific) Low-medium flow, suitable for blow molding, injection molding, extrusion. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527-2 |
Styron CALIBREâ„¢ 280-25 Polycarbonate CALIBREâ„¢ PC Utility Grade 280-15 is a high flow opaque polycarbonate with an internal mold release system. Applications: Internal parts Electrical Electronics Lightning Information provided b.. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
Styron CALIBREâ„¢ 301-15 Polycarbonate Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527-2 |
Styron CALIBREâ„¢ 7100-15 Polycarbonate CALIBREâ„¢ 7100-15 glass-reinforced resin offers increased modulus and improved heat distortion resistance, with minimal shrinkage. It also offers outstanding UL-94 flammability ratings. CALIBR.. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX973 PPE+PA NORYL GTX973 is a material especially designed for electrostatic painting and powder coating applications. The material combines high heat resistance with impact and conductivity in a unique way. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
Styron CALIBREâ„¢ 303-10 Polycarbonate Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-2/50 |
Styron CALIBREâ„¢ 303-15 Polycarbonate Resin Overview: CALIBREâ„¢ 300-115 polycarbonate resins offer exceptional impact resistance, heat distortion resistance and optical clarity. The CALIBREâ„¢ 300-10 series products are available in 4 .. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | 0.125 in, injection molded, unannealed; ASTM D638 |
Styron EMERGEâ„¢ 4330-6 Polycarbonate EMERGEâ„¢ PC 4330-6 advanced resin is a polycarbonate resin offering ultraviolet light stability, high heat resistance and maximum toughness. Applications: Consumer Electronics and Information .. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | parallel; ISO 527-3 |
Covestro Desmopan® DP 3055D Polyurethane injection molding gradewith high mechanical strength for articles subject to wearexcellent abrasion resistancegood wear resistancevery short cycle timesApplicationInjection molded engineering partsR.. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 |
Covestro Makroblend® DP UT5007 Polycarbonate + PBT, Impact Grade Developmental product(PC+PBT)-blendimpact modifiedeasy releaseUV-stabilizedinjection molding grade Makroblend DP UT5007* provides an outstanding balance of low-temperature impact strength and flow.. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 |
DSM Akulon® S223-D Nylon 66 (European Grade) (Cond) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 |
DuPont Performance Polymers Crastin® CE2055 BK580 Polybutylene Terephthalate (PBT) Unreinforced Low Viscosity Polybutylene Terephthalate Crastin CE2055 is an unreinforced low viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performanc.. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | |
Dow SiLK™ I 1070 Semiconductor Dielectric Resin SiLK™ I 1070 is designed for easy integration and extendibility, and its formulations offer a robust feature set. High thermal stability and fracture toughness means SilK™ I 1070 is compatible wi.. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | |
Dow SiLK™ I 130 Semiconductor Dielectric Resin SiLK™ I 130 is designed for easy integration and extendibility, and its formulations offer a robust feature set. High thermal stability and fracture toughness means SilK™ I 130 is compatible with.. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 |
DSM Akulon® S223-D (Cond.) Nylon 66 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50mm/min; ASTM D638 |
LG Chemical Lupoy 1302HP-07 Polycarbonate Resin Description: LUPOY PC 1302HP-07 resin is designed for extrusion products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Characteristics.. |