PolyOne Edgetek® X TR2-10GF/000 NATURAL Copolyester

Category	Polymer , Thermoplastic , Polyester, TP
Manufacturer	PolyOne Corporation
Trade Name	Edgetek®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Edgetek® X TR2-10GF/000 NATURAL Copolyester.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The Edgetek™ engineering thermoplastics compounds made with Eastman Tritan™ copolyester offer a wide range of performance and properties with the addition of reinforcing additives. By utilizing Eastman Tritan™ copolyester these compounds provide chemical resistance, clarity, heat resistance and BPA-free solutions.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.25 g/cc	1.25 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm @Thickness 3.18 mm	0.0020 - 0.0030 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	53.1 MPa	7700 psi	Type I, 5.1 mm/min; ASTM D638
Tensile Strength, Yield	60.0 MPa	8700 psi	5.1 mm/min; ASTM D638
Elongation at Break	13 %	13 %	Type I, 5.1 mm/min; ASTM D638
Elongation at Yield	5.0 %	5.0 %	5.1 mm/min; ASTM D638
Tensile Modulus	2.76 GPa	400 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	103 MPa	14900 psi	1.3 mm/min; ASTM D790
Flexural Modulus	2.76 GPa	400 ksi	1.3 mm/min; ASTM D790
Izod Impact, Notched	0.530 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	0.993 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A
Izod Impact, Unnotched	9.60 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	18.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	120 µm/m-°C @Temperature -30.0 - 30.0 °C	66.7 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM E831
CTE, linear, Transverse to Flow	200 µm/m-°C @Temperature -30.0 - 30.0 °C	111 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM E831
Deflection Temperature at 0.46 MPa (66 psi)	116 °C @Thickness 3.18 mm	241 °F @Thickness 0.125 in	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	108 °C @Thickness 3.18 mm	226 °F @Thickness 0.125 in	Unannealed; ASTM D648

Processing Properties	Metric	English
Melt Temperature	266 - 282 °C	511 - 540 °F
Mold Temperature	60.0 - 65.6 °C	140 - 150 °F
Drying Temperature	87.8 °C	190 °F
Dry Time	4.00 hour	4.00 hour

Descriptive Properties	Value	Comments
Features	BPA Free
	Crazing Resistant
	Filled
	Good Chemical Resistance
	Good Crack Resistance
	Good Dimensional Stability
	Good Toughness
	Medium Clarity
	Medium Heat Resistance
Filler / Reinforcement	Glass Fiber Reinforcement
Forms	Pellets
Generic Material	Copolyester
Generic Name	Copolyester
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Appliance Components
	Consumer Applications
	Food Service Applications
	Household Goods
	Industrial Applications
	Transparent or Translucent Parts