- Polymer Property : Tensile Strength, Yield = 98.0 MPa
Polymer Property : Tensile Strength, Yield = 98.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | ASTM D638 |
| NOVA Chemicals Dylark® 238P20 High Performance Glass Filled Styrenic Very high modulus, High heat resistance, Excellent flow characteristics, Excellent adhesion to urethaneApplications: Instrument panel substrates, consoles, Cluster housing, interior trimInjection Sp.. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | ISO value at 50 mm/min. |
| BASF Capron® HPN 9333G Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron HPN 9333G is a 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface a.. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | ISO 527 |
| Victrex® PEEK 450G General Purpose Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and extrusion, standard flow, FDA food contac.. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | ISO 527 |
| Victrex® PEEK 450PF Fine Powder Grade Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, fine powder for compression molding, standard flow, FDA food contact complia.. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | ISO 527-1/-2 |
| Lanxess Durethan® DP A 32 901510 Nylon 66 PA 66 standard injection molding grade, non-reinforced, very easy release |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp GFL14 PSU LNP* Lubricomp* GFL14 is a compound based on Polysulfone containing Glass Fiber and PTFE Lubricant.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Ultem DT1800E PEI Blend Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Americas re.. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Ultem DT1800E PEI Blend (Asia Pacific) Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacifi.. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Ultem DT1810E PEI Blend Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Americas re.. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Ultem DT1810E PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacifi.. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Ultem DT1810E PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Afri.. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics ULTEM DT1810EV PEI Blend Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics ULTEM DT1810EV PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Ultem DT1810EV PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed.This data was supplied by SABIC-IP for.. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics ULTEM EXUM0169 PEI Blend Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics ULTEM EXUM0169 PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Ultem EXUM0169 PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Afri.. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
| SABIC Innovative Plastics Noryl GFN2L PPE+HIPS (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
| SABIC Innovative Plastics NORYL GFN2L PPE+PS (Asia Pacific) PPE+PS GF20%, hydrolytic stability |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
| SABIC Innovative Plastics NORYL NC220 PPE+HIPS (Asia Pacific) |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
| SABIC Innovative Plastics NORYL CN1134 PPE+PS (Asia Pacific) 20% filled FR high modulus PPE/PS blend |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP (Europe-Africa-Middle East) Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | ISO 527-2 |
| Ascend Performance Materials Vydyne® 20NSP Nylon 66, DAM Vydyne® 20NSP is a general-purpose, highly nucleated, lubricated PA66 resin available in natural color. It is designed to crystallize rapidly in order to reduce cycle times and increase productivit.. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | ISO value at 50 mm/min. |
| BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron HPN 9333G HS is a heat stabilized, 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with.. |
|||
| Tensile Strength, Yield | 98.0 - 220 MPa | 14200 - 31900 psi | Average value: 163 MPa Grade Count:15 |
| Overview of materials for Polyetheretherketone, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Glass Fiber Filled". Each property range of values reported is minimum and maximum.. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
| SABIC Innovative Plastics NORYL PX2922 PPE (Asia Pacific) GF20% FR-V0 |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
| SABIC Innovative Plastics Valox® VC108 PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
| SABIC Innovative Plastics Lexan® LC108 PC (Asia Pacific) Polycarbonate base, 8% carbon fiber reinforced, FR |
|||