SABIC Innovative Plastics Valox® VC108 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® VC108 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D 792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| 0.0080 - 0.010 cm/cm @Thickness 6.40 mm |
0.0080 - 0.010 in/in @Thickness 0.252 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
| Elongation at Break | 3.0 % | 3.0 % | SABIC - Japan Method |
| Flexural Strength | 148 MPa | 21500 psi | ASTM D 790 |
| Flexural Modulus | 5.98 GPa | 867 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.390 J/cm @Temperature 23.0 °C |
0.731 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
44.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+8 - 1.00e+12 ohm | 1.00e+8 - 1.00e+12 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Advanced Elastomer Systems Trefsin® 3201-65 W305 Thermoplastic Rubber (discontinued **)
- Styrolution Terluran® HH-112 Q42 Gray 10072 ABS
- Total PPH M3865 Metallocene Isostatic Propylene Polymer, Fiber Grade
- A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene
- ChevronTexaco 5606G Aircraft Hydraulic Oil
- CIMBAR MV 610 Talc
- CENTROPLAST CENTROMID 12 soft Polyamide 12 soft
- Huntsman Rexell® M3107 Blown Film Extrusion LLDPE (discontinued **)
- DuPont Elvax® 3134Q Ethylene-Vinyl Acetate Copolymer Resin for Extrusion Coating, Casting (discontinued **)&l
Copyright © lookpolymers.com All Rights Reserved