SABIC Innovative Plastics NORYL CN1134 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL CN1134 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% filled FR high modulus PPE/PS blend
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0025 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0025 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 22.1 g/10 min @Load 2.16 kg, Temperature 300 °C |
22.1 g/10 min @Load 4.76 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
| Elongation at Break | 7.0 % | 7.0 % | SABIC - Japan Method |
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| Flexural Modulus | 5.88 GPa | 853 ksi | ASTM D790 |
| Izod Impact, Notched | 0.680 J/cm | 1.27 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 - 35.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.9 - 19.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C @Thickness 6.40 mm |
223 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- RheTech Products T40P105-01 40% Talc Reinforced Polypropylene, Black
- Polykemi AB POLYfill PPC GF7020 PD2 E15 Polypropylene Copolymer, Glass Fiber Reinforced, Chemically Coupled
- LNP Thermocomp® EC-1006 EM Polyetherimide, Carbon Fiber Reinforcement (discontinued **)
- Michelman® Michem® Emulsion 37135 Nonionic polyethylene emulsion
- Taiwan Sheen Soon Sheenthane® AH-780 TPU for Hotmelt Adhesive
- Polyram PlusTek PA700BL10 Nylon 6.6 for Injection Molding, UV Stabilized
- Polyplastics Duranex® 407EP Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance
- ChevronTexaco EDM Fluid
- Dow Hydroxyethyl Acrylate
- Ashley Polymers Ashlene® 291WO PPO
Copyright © lookpolymers.com All Rights Reserved