Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
Polymer Industries Densetec PP Homopolymer Sheet Polymer Industries’ Densetec Homopolymer Polypropylene exhibits the properties of high corrosion resistance, high temperature resistance, and great tensile strength. It maintains its stiffness at e.. |
|||
Tensile Strength, Yield | >= 33.0 MPa | >= 4790 psi | ASTM D638 |
NIZHNEKAMSKNEFTEKHIM PP 1500N (F30G) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO 527-2 |
Polyplastic Armlen® PP MF 25-3-901 Polypropylene, 20% Mineral Filled Heat stabilized, black colorInformation provided by PolyPlastic Group. |
|||
Tensile Strength, Yield | 33.0 - 108 MPa | 4790 - 15600 psi | Average value: 46.4 MPa Grade Count:125 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded". Each property range of values reported i.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 mm/min |
Polimeri Europa SINKRAL C333/m² ABS, Heat Stabilized
(discontinued **) Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,105-04-16-20 Special low gloss grade for injection moulding which combines medium heat resistance with a good b.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO 527-1, -2 |
LyondellBasell Hostacomâ„¢ BC142/1AC Polypropylene Copolymer Description: Hostacomâ„¢ BC142/1AC conventional melt flow, 3,600 MPa flexural modulus, precolored, mineral-filled polypropylene copolymer has a good balance of stiffness and impact resistance. It.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DZL34E PC (Asia Pacific) LNP* Lubricomp* DZL34E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Valox® 308 PBT PBT, For compounding only. Not intended for Injection Molding. Melt viscosity: 250C at 21.6 kgf is 3500-4500.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 2 in/min; ASTM Test |
Styrolution Luran® S 776 SE ASA Luran S 776 SE is a general purpose extrusion ASA grade with good toughness and strength, used for sheet and profile extrusions.Information provided by STYROLUTION, which is a joint venture between .. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
Tipco Tipcolene® CR 8233 - 20% Talc/Mineral Reinforced Polypropylene Copolymer Compound 20% Mineral Reinforced PP CopolymerApplications: Automotive Pillars & TrimsProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 cm/min; ASTM D638 |
Washington Penn PPUP4G402 Polypropylene, 40% Talc Filled, High Flow Exceptional retention of mechanical properties and appearance upon long term heat aging.Applications: Appliance parts.Data provided by Washington Penn Plastic Co., Inc. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO 527-2 |
Total PPH 4030 Polypropylene Homopolymer Polypropylene PPH 4030 is a homopolymer polypropylene with a Melt Flow index of 3 g/10 min.Polypropylene PPH 4030 has been designed for the production of BOPP film with the tenter frame process. Th.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO 527-2 |
Total PPH 4054 Polypropylene Homopolymer Polypropylene PPH 4054 is a homopolymer polypropylene with a Melt Flow index of 3 g/10 min.Polypropylene PPH 4054 has been designed for the production of BOPP film with the tenter frame process. Th.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
Total PSI 3441 High Heat Resistance Impact Polystyrene Total Petrochemicals Polystyrene 3441 is a high heat resistance, high impact polystyrene for injection molding. It is recommended for the manufacturing of articles which require good dimensional st.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | GB/1040 |
Zhejiang Juner PP8 PP For Automotive Parts Applications: Air Conditioning SystemInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 79% Ret. |
UBE UBESTA® 3030U Nylon 12 (After Toluene for 500 hours) Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, c.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 2.0 in/min; ASTM D638 |
ExxonMobil PP7905E1 Polypropylene Homopolymer Product Description: A high crystallinity, low impact strength copolymer resin designed for compounding base or injection molding applications requiring very high melt flow rate.Availability: North.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
Dow DX5E66 Polypropylene Homopolymer Resin OverviewConsistent processabilityVery high cleanlinessGood optical propertiesComplies with U.S. FDA 21 CFR 177.1520 (c)1.1a, EU-Directive 2002/72/EC, Canadian HPFB No ObjectionDX5E66 Developmental P.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® RS LC1610 BK387 Nylon 1010
(Unverified Data**) Plasticized Toughened Renewably Sourced Polyamide 1010 Developed for Extrusion Information provided by DuPont Performance Polymers |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO R527 |
Arkema Group Orgalloy® LE 60XV Polyamide 6 Alloy Polyamide Alloy, Semi-Flexible grade, Nylon 6 basedTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 mm/min |
Arkema Group Rilsan® MA 4420 Nylon 12, Flexible Tubing Grade (Dry) Designation ISO 1874-PA12-HI,EHL,22-003Flexible grade for tubes extrusion. Available color: black. Light and heat stabilized.Flexibility. High burst pressure and impact strength. Fit for use in a wi.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 mm/min |
Arkema Group Rilsan® MB 3501 Nylon 11, Flexible Tubing Grade (Dry) Designation ISO 1874-PA11-HI,MHL,22-004Flexible grade for tubes extrusion. Available color: black. Light and heat stabilized.Flexibility. High burst pressure and impact strength. Fit for use in a wi.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO R 527 |
Addiplast Addilene H 242 M40 Polypropylene Homopolymer High heat resistance, detergent stabilizedInformation provided by Addiplast. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO R 527 |
Addiplast Addilene J 110 Polypropylene Copolymer UnreinforcedInformation provided by Addiplast. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 mm/min; ASTM D638 |
Carmel Olefins CAPILENE® G 65 F Polypropylene Homopolymer Description: CAPILENE® G 65 F is a polypropylene homopolymer designed for the production of biaxially oriented polypropylene films (BOPP). It exhibits good processability, easy film stretchabilit.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO value at 50 mm/min. |
BASF Capron® 8351 Impact Modified Nylon 6 (Conditioned)
(discontinued **) Capron 8351 is a type 6 polyamide graft copolymer developed for injection molding applications requiring a high level of toughness combined with moderate flexibility and faster cycles. It is also .. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
Braskem H 401 Cast Film Extrusion Polypropylene Description: H 401 is a medium melt flow rate homopolymer polypropylene, additived with slip and antiblocking agents. Designed specially for cast film. This product features good impact strength, ex.. |
|||
Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO 527-2 |
Polyplastic Armlen® PP MF 20-3-901 Polypropylene, 20% Mineral Filled Heat stabilized, low emission, black colorInformation provided by PolyPlastic Group. |