- Washington Penn PPUP4G402 Polypropylene, 40% Talc Filled, High Flow
Washington Penn PPUP4G402 Polypropylene, 40% Talc Filled, High Flow
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Washington Penn |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Washington Penn PPUP4G402 Polypropylene, 40% Talc Filled, High Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Exceptional retention of mechanical properties and appearance upon long term heat aging.Applications: Appliance parts.Data provided by Washington Penn Plastic Co., Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Melt Flow | 4.5 - 7.5 g/10 min | 4.5 - 7.5 g/10 min | Cond L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 cm/min; ASTM D638 |
| Elongation at Break | 10 % | 10 % | 50 cm/min; ASTM D638 |
| Flexural Yield Strength | 58.0 MPa | 8410 psi | ASTM D790 |
| Flexural Modulus | 3.60 GPa | 522 ksi | Tangent; ASTM D790 |
Users viewing this material also viewed the following:
- Magyar Aluminum ALOLT 38AF Aluminum Hydroxide
- Haynes Hastelloy® S alloy, flat products
- Spartech Royalite R57 FR/ABS Aircraft Grade Sheet
- SK Chemicals SKYPEL G140D General Grade
- Shakespeare WN-38 diameter 0.4 mm Nylon 6 Monofilament
- Teijin Panlite® GV-3430R High Flame Retardancy, Glass Fiber Reinforced Polycarbonate Resin
- A. Schulman POLYBLAK™ 4479-01A Black Color Concentrate, 50% Carbon Black Based In Polyethylene
- Fainplast Compounds PM 100 Flexible PVC, Extrusion
- Arkema Group Pebax® MX 1283 Polyether Block Amide (PEBA) (Conditioned)
- Loctite® PRISM® 401 Instant Adhesive
Copyright © lookpolymers.com All Rights Reserved