DuPont Performance Polymers Zytel® RS LC1610 BK387 Nylon 1010  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon
Manufacturer DuPont Performance Polymers
Trade Name Zytel® RS
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® RS LC1610 BK387 Nylon 1010  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plasticized Toughened Renewably Sourced Polyamide 1010 Developed for Extrusion Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
DAM; ISO 1183
Water Absorption 1.5 %

@Thickness 2.00 mm
 1.5 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 0.750 %

@Thickness 2.00 mm
 0.750 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity 210000 cP

@Temperature 250 °C
 210000 cP

@Temperature 482 °F
 DAM; @ 1000 sec-1; ISO 11443
104300 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 104300 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
116800 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
 116800 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
 ISO 11403-1 -2
145200 cP

@Shear Rate 5000 1/s,
Temperature 220 °C
 145200 cP

@Shear Rate 5000 1/s,
Temperature 428 °F
 ISO 11403-1 -2
402600 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 402600 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
453400 cP

@Shear Rate 500 1/s,
Temperature 230 °C
 453400 cP

@Shear Rate 500 1/s,
Temperature 446 °F
 ISO 11403-1 -2
513700 cP

@Shear Rate 500 1/s,
Temperature 220 °C
 513700 cP

@Shear Rate 500 1/s,
Temperature 428 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.016 cm/cm
0.016 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Stress 0.760 MPa

@Strain 0.250 %,
Temperature 90.0 °C
 110 psi

@Strain 0.250 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
1.25 MPa

@Strain 0.700 %,
Temperature 150 °C
 181 psi

@Strain 0.700 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
1.43 MPa

@Strain 0.190 %,
Temperature 23.0 °C
 207 psi

@Strain 0.190 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
1.53 MPa

@Strain 0.500 %,
Temperature 90.0 °C
 222 psi

@Strain 0.500 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
3.23 MPa

@Strain 2.56 %,
Temperature 150 °C
 468 psi

@Strain 2.56 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
6.01 MPa

@Strain 0.250 %,
Temperature -20.0 °C
 872 psi

@Strain 0.250 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
6.44 MPa

@Strain 0.500 %,
Temperature 0.000 °C
 934 psi

@Strain 0.500 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
7.09 MPa

@Strain 1.78 %,
Temperature 40.0 °C
 1030 psi

@Strain 1.78 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
7.29 MPa

@Strain 1.30 %,
Temperature 40.0 °C
 1060 psi

@Strain 1.30 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
8.00 MPa

@Strain 0.280 %,
Temperature -40.0 °C
 1160 psi

@Strain 0.280 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
8.70 MPa

@Strain 21.27 %,
Temperature 150 °C
 1260 psi

@Strain 21.27 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
9.31 MPa

@Strain 17.89 %,
Temperature 150 °C
 1350 psi

@Strain 17.89 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
9.50 MPa

@Strain 42.34 %,
Temperature 150 °C
 1380 psi

@Strain 42.34 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
13.53 MPa

@Strain 0.660 %,
Temperature -20.0 °C
 1962 psi

@Strain 0.660 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
15.42 MPa

@Strain 17.42 %,
Temperature 90.0 °C
 2236 psi

@Strain 17.42 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
16.23 MPa

@Strain 17.13 %,
Temperature 90.0 °C
 2354 psi

@Strain 17.13 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
18.68 MPa

@Strain 0.700 %,
Temperature -40.0 °C
 2709 psi

@Strain 0.700 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
22.79 MPa

@Strain 18.65 %,
Temperature 40.0 °C
 3305 psi

@Strain 18.65 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
24.64 MPa

@Strain 3.76 %,
Temperature 23.0 °C
 3574 psi

@Strain 3.76 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
26.27 MPa

@Strain 17.4 %,
Temperature 40.0 °C
 3810 psi

@Strain 17.4 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
28.55 MPa

@Strain 36.74 %,
Temperature 40.0 °C
 4141 psi

@Strain 36.74 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
30.77 MPa

@Strain 19.45 %,
Temperature 23.0 °C
 4463 psi

@Strain 19.45 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
34.12 MPa

@Strain 2.29 %,
Temperature 0.000 °C
 4949 psi

@Strain 2.29 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
37.22 MPa

@Strain 26.34 %,
Temperature 23.0 °C
 5398 psi

@Strain 26.34 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
45.01 MPa

@Strain 17.39 %,
Temperature 0.000 °C
 6528 psi

@Strain 17.39 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
52.51 MPa

@Strain 14.94 %,
Temperature 0.000 °C
 7616 psi

@Strain 14.94 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
58.21 MPa

@Strain 2.98 %,
Temperature -20.0 °C
 8443 psi

@Strain 2.98 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
63.58 MPa

@Strain 4.37 %,
Temperature -20.0 °C
 9222 psi

@Strain 4.37 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
67.5 MPa

@Strain 3.06 %,
Temperature -40.0 °C
 9790 psi

@Strain 3.06 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
68.27 MPa

@Strain 3.17 %,
Temperature -40.0 °C
 9902 psi

@Strain 3.17 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
69.51 MPa

@Strain 10.19 %,
Temperature -20.0 °C
 10080 psi

@Strain 10.19 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
74.54 MPa

@Strain 6.66 %,
Temperature -20.0 °C
 10810 psi

@Strain 6.66 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
87.19 MPa

@Strain 6.11 %,
Temperature -40.0 °C
 12650 psi

@Strain 6.11 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
89.38 MPa

@Strain 7.42 %,
Temperature -40.0 °C
 12960 psi

@Strain 7.42 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
Tensile Strength, Yield 33.0 MPa
4790 psi
50%RH; ISO 527-1/-2
35.0 MPa
5080 psi
DAM; ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
DAM; Nominal; ISO 527-1/-2
>= 50 %
>= 50 %
50%RH; Nominal; ISO 527-1/-2
Elongation at Yield 32 %
32 %
DAM; ISO 527-1/-2
39 %
39 %
50%RH; ISO 527-1/-2
Tensile Modulus 0.570 GPa
82.7 ksi
50%RH; ISO 527-1/-2
0.790 GPa
115 ksi
DAM; ISO 527-1/-2
0.189 GPa

@Temperature 120 °C
 27.4 ksi

@Temperature 248 °F
 50%RH; ISO 11403-1 -2
0.194 GPa

@Temperature 120 °C
 28.1 ksi

@Temperature 248 °F
 DAM; ISO 11403-1 -2
0.374 GPa

@Temperature 40.0 °C
 54.2 ksi

@Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.458 GPa

@Temperature 40.0 °C
 66.4 ksi

@Temperature 104 °F
 DAM; ISO 11403-1 -2
2.68 GPa

@Temperature -40.0 °C
 389 ksi

@Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
2.782 GPa

@Temperature -40.0 °C
 403.5 ksi

@Temperature -40.0 °F
 DAM; ISO 11403-1 -2
Flexural Strength 19.0 MPa
2760 psi
50%RH; ISO 178
24.0 MPa
3480 psi
DAM; ISO 178
19.0 MPa

@Strain 3.50 %
 2760 psi

@Strain 3.50 %
 50%RH; ISO 178
24.0 MPa

@Strain 3.50 %
 3480 psi

@Strain 3.50 %
 DAM; ISO 178
Shear Strength 0.059185 MPa

@Shear Rate 50.0 1/s,
Temperature 240 °C
 8.5841 psi

@Shear Rate 50.0 1/s,
Temperature 464 °F
 ISO 11403-1 -2
0.067205 MPa

@Shear Rate 50.0 1/s,
Temperature 230 °C
 9.7473 psi

@Shear Rate 50.0 1/s,
Temperature 446 °F
 ISO 11403-1 -2