Arkema Group Orgalloy® LE 60XV Polyamide 6 Alloy
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® LE 60XV Polyamide 6 Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide Alloy, Semi-Flexible grade, Nylon 6 basedTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO R1183 |
| Water Absorption | 0.70 % | 0.70 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 23°C / 50% RH; ISO 62 |
| 5.5 % | 5.5 % | in 23°C water; ISO 62 | |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 235 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ISO 868 |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ISO R527 |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO R527 |
| Elongation at Break | >= 250 % | >= 250 % | ISO R527 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO R527 |
| Modulus of Elasticity | 0.800 GPa | 116 ksi | ISO R527 |
| Flexural Strength | 17.5 MPa | 2540 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| Flexural Modulus | 0.690 GPa | 100 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| Charpy Impact, Notched | 4.00 J/cm² | 19.0 ft-lb/in² | After conditioning at 23°C/50%RH; ISO 179/Af |
| 1.20 J/cm² @Temperature -20.0 °C |
5.71 ft-lb/in² @Temperature -4.00 °F |
After conditioning at 23°C/50%RH; ISO 179/Af |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO R1218 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GF 35 Polyamide 66, 35% Glass Fiber
- Overview of materials for Nylon 6/69
- Iran Petrochemical (PCC) PC 0407 Polycarbonate
- Teknor Apex APEX® 4011 Polyvinyl Chloride, Flexible
- Polyram PlusTek PA862 Nylon 6.6 for Injection Molding, High Impact Modified
- Total PPC 3640 Polypropylene, Heterophasic Copolymer
- DuPont™ Surlyn® 1601-2LM Sodium Ionomer Resin for Blown and Cast Film
- Entec Hypro™ PPC-CC10 Natural Copolymer Polypropylene, 10% Calcium Carbonate Filled
- Epoxy Technology EPO-TEK® H20-FC Electrically Conductive Epoxy
- DuPont Performance Polymers Zytel® LC6601 BK551 Nylon 612 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved