Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 160 MPa | 23200 psi | 50 mm/min; ASTM D638 |
Ovation Polymers UTTAP QU HT530 GF Nylon, 30% Glass Reinforced Glass reinforced (30 %) - High Temperature Polyamide Alloy, excellent chemical and electrical resistance, high stiffness, modulus and HDT. *All properties are measured after 48 hours of conditioning.. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | ISO 527-2/5 |
PolyOne Nymax™ GF 1800 35 HS Natural Polyamide 612 (Nylon 612) Property data for molded test bars: Dry as MoldedInformation provided by PolyOne |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | ASTM D638 |
LNP Stat-Kon® LC-1003 EM Polyetheretherketone, Carbon Fiber Reinforcement
(discontinued **) Features: Good Moldability, Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; howev.. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | ISO 527, ASTM D638 |
Nilit Nilamid A3 H6 G6 30% Glass Reinforced PA66 Description: Nilamid A3 H6 G6 is a 30% glass fiber reinforced NYLON 66 with a special stabilization system against hot oil and grease. As a result of this stabilization, the material has a brown nat.. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | ISO 527, ASTM D638 |
Nilit Nilamid A3 H7 G6 30% Glass Reinforced PA66 Description: Nilamid A3 H7 G6 is a 30% glass fiber reinforced NYLON 66 with a high heat stabilization. This product combines good overall mechanical performance and impact strength with ease of proc.. |
|||
Tensile Strength, Yield | 160 MPa @Temperature 22.0 °C |
23200 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 1800 Unsaturated Polyester UP SMC 1800 is for structural applications requiring extreme high mechanical properties and low weight. These compounds mould to parts focussing on mechanical strength for replacement of metals in ord.. |
|||
Tensile Strength, Yield | 160 MPa @Strain 0.200 %, Temperature 980 °C |
23200 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes 25 alloy, vacuum investment castings, solution treated Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36U PA 66 LNP* LUBRICOMP* RFL36U is a compound based on Nylon 66 resin containing 15% PTFE, 30% Glass Fiber. Added features of this grade include: Wear Resistant, UV Stabilized. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 2310EPR PEI 30% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 2310EPR PEI (Asia Pacific) 30% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® V9290 PET (Europe-Africa-Middle East) 45% GF PET, Glass, Mold Release, Heat Stabilized, |
|||
Tensile Strength, Yield | 160 MPa @Strain 0.200 %, Temperature 300 °C |
23200 psi @Strain 0.200 %, Temperature 572 °F |
Annealed prior to test |
Special Metals NILO® Alloy 48 Controlled-Expansion Alloy Inflection point 460°C. A nickel-iron controlled-expansion alloy containing 48% nickel. Its coefficient of thermal expansion is designed to match that of soft lead and soda-lime glasses. The a.. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | ASTM-D638 |
Polyram PlusTek PB300G5 Nylon 6, 15% Glass Fiber 15% glass-fiber reinforced, heat stabilized polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | ISO 527 |
Polyram PlusTek PB315G33 Nylon 6 for Injection Molding, 33% Glass Fiber Reinforced, UV and Heat Stabilized 33% Glass fiber reinforced, UV and heat stabilized Nylon 6 for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | ISO 527 |
Polyram PlusTek RA331G6 Nylon 66 for Injection Molding, 30% Glass-Fiber Reinforced 30% Glass-fiber reinforced Nylon 66 for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | ASTM D638 |
E-Polymers TEKAMID® TA210GR , 33% Glass Fiber Reinforced PA66, DAM 33% Glass Fiber reinforced, Anti EG, Anti HydrolysisInformation provided by E-Polymers Co. Ltd. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | ASTM D638, ISO R527 |
EPICHEM PA 6 GF 30 Polyamide 6, 30% Glass Characteristics: medium viscosity, 30% glass fibre filled |
|||
Tensile Strength, Yield | >= 160 MPa | >= 23200 psi | |
Aleris Alustar Aluminum Alloy, MIG-welded At least 20% stronger than AA 5083 before and after welding. Bendability and weldability similar to AA 5083. High corrosion resistance. Provides options for ship design and building.Composition d.. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® B3EG5 25% Glass Filled PA6 (Dry) Description: 25% glass-fiber reinforced injection-molding grade for industrial articles and electrical insulating partsInformation provided by BASF |
|||
Tensile Strength, Yield | >= 160 MPa | >= 23200 psi | ASTM D882 |
CEN® Electronic Material CF 150CF019 Polyimide Film CEN®CF polyimide film is the general CEN®CN film that is coated or laminated on one or both sides with Teflon® FEP fluoropolymer. CEN®CF imparts heat sealability, provides a moisture barrier, an.. |
|||
Tensile Strength, Yield | >= 160 MPa | >= 23200 psi | ASTM D882 |
CEN® Electronic Material CF 200CF919 Polyimide Film CEN®CF polyimide film is the general CEN®CN film that is coated or laminated on one or both sides with Teflon® FEP fluoropolymer. CEN®CF imparts heat sealability, provides a moisture barrier, an.. |
|||
Tensile Strength, Yield | 160 - 170 MPa @Strain 0.200 % |
23200 - 24700 psi @Strain 0.200 % |
|
AMT AM-Lite® Die Casting Magnesium Alloy AM-lite is a high surface finish die casting alloy suitable for applications that currently utilize zinc, aluminum or magnesium (alloy AZ91D) die castings, or plastic injection moldings. AM-lite has.. |
|||
Tensile Strength, Yield | >= 160 MPa | >= 23200 psi | |
Aleris Alustar Aluminum Alloy, O/H111 At least 20% stronger than AA 5083 before and after welding. Bendability and weldability similar to AA 5083. High corrosion resistance. Provides options for ship design and building.Composition d.. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | 50mm/min; ISO 527 |
BASF Ultramid® A3X2G7 35% Glass Filled PA66 (Dry) Ultramid A3X2G7 is a 35% glass fiber reinforced injection molding PA66 grade with improved flame retardance and enhanced long-term stability. Flame retardant based on red phosphorus; very high stif.. |
|||
Tensile Strength, Yield | >= 160 MPa | >= 23200 psi | ASTM D882 |
CEN® Electronic Material CF 120CF616 Polyimide Film CEN®CF polyimide film is the general CEN®CN film that is coated or laminated on one or both sides with Teflon® FEP fluoropolymer. CEN®CF imparts heat sealability, provides a moisture barrier, an.. |
|||
Tensile Strength, Yield | 160 - 200 MPa | 23200 - 29000 psi | |
ArcelorMittal 54 High formability steel for drawing, Cold rolled Available in the following: Extragal®/Galvannealed (DX54D +Z/+ZF)Description: This range of non-alloyed mild steels is designed for deep and extra deep drawing applications. These products are used.. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | ASTM D638 |
Gharda Chemicals GATONE™ 5330GF Polyetheretherketone (PEEK)
(discontinued **) Characteristics: Outstanding Chemical Resistance Outstanding Wear Resistance Outstanding Resistance to HydrolysisExcellent Mechanical Properties Outstanding Thermal properties Very good Dielectric.. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® B3WG5 25% Glass Filled PA6 (Dry) Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el.. |
|||
Tensile Strength, Yield | 160 MPa | 23200 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® B3WG5 BK 00654 PA6 25% Glass Filled BK (Dry) Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el.. |