LNP Stat-Kon® LC-1003 EM Polyetheretherketone, Carbon Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Stat-Kon® LC-1003 EM Polyetheretherketone, Carbon Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Good Moldability, Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.33 g/cc
1.33 g/cc
Method A; ASTM D792
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 160 MPa
23200 psi
ASTM D638
Tensile Strength, Yield 160 MPa
23200 psi
ASTM D638
Elongation at Break 1.8 %
1.8 %
ASTM D638
Elongation at Yield 1.8 %
1.8 %
ASTM D638
Tensile Modulus 11.5 GPa
1670 ksi
ASTM D638
Flexural Strength 255 MPa
37000 psi
ASTM D790
Flexural Modulus 9.51 GPa
1380 ksi
ASTM D790
Izod Impact, Notched 0.374 J/cm

@Thickness 3.18 mm
0.701 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 4.00 J/cm

@Thickness 3.18 mm
7.49 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 4.30 kJ/m²
2.05 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 29.3 kJ/m²
13.9 ft-lb/in²
ISO 180
Falling Dart Impact 4.40 J
3.25 ft-lb
ASTM D3763
Impact Test 1.80 J
1.33 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 1000 - 1.00e+7 ohm
1000 - 1.00e+7 ohm
ASTM D4496
Processing Properties Metric English Comments
Melt Temperature 379 - 388 °C
714 - 730 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.010 %
0.010 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi