Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 125 MPa | 18100 psi | |
Osprey Metals CE11 Al-Si Controlled Expansion Alloy Al-50%Si controlled expansion alloy manufactured and patented by Osprey Metals Ltd.Information provided to MatWeb by Osprey Metals. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | |
Radici Radilon® S RCV3015 (dry) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | ISO 527-1/2 |
Radici Raditer® BRV300 Polybutylene Terephthalate PBT Glass Fiber ReinforcedInformation provided by Radici group. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | ISO 527, ASTM D638 |
Nilit Nilamid A G5 FR C4 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Halogens) Description: Nilamid A G5 FR C4 combines excellent mechanical performance with flame retardancy. The halogenated flame retardant system used in this product allows a wide range of colors. This produ.. |
|||
Tensile Strength, Yield | 125 MPa @Temperature -40.0 °C |
18100 psi @Temperature -40.0 °F |
ISO 527 |
BASF Capron® 8200 NL Nylon 6 (DAM)
(discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line. |
|||
Tensile Strength, Yield | 125 MPa @Temperature -40.0 °C |
18100 psi @Temperature -40.0 °F |
ASTM D638 |
BASF Capron® 8202 NL Nylon 6 (DAM)
(discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | ASTM D638 |
LG Chemical Lupox® GP-2301F General Purpose PBT, 30% Glass Fiber Reinforced, Flame Retardant LUPOX semi-crystalline thermoplastic PBT resins exhibit properties including high strength, rigidity and good resistance to fatigue and creep at elevated temperatures. Furthermore, LUPOX resins sho.. |
|||
Tensile Strength, Yield | >= 125 MPa | >= 18100 psi | |
MetalTek MTEK CZ-100 Cast UNS N02100 Severe Corrosion and Heat Resistant Alloy Strong, tough and resistant to a wide range of industrial chemicals.Applications: Process equipment; food, pharmaceutical and chemical.Information provided by MetalTek |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® DP 2037/30 H2.0 LT 904040 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, black colored for laser transmission-welding (laser-transparent), good heat-ageing resistance |
|||
Tensile Strength, Yield | 125 MPa @Strain 0.200 %, Temperature 980 °C |
18100 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | ASTM D638 |
Techmer ES HiFill FR® PA6 GF33 FR HS L 33% Glass Filled (Conditioned) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Flame Retardant, Heat Stabilized and Lu.. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DEL139P PC LNP* STAT-KON* DEL139P is a compound based on Polycarbonate containing 15% Carbon Fiber, 5% PTFE. Added features of this grade include: Electrically Conductive, Exceptional Processing, Flame Retar.. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Stat-kon OE002 PPS LNP* Stat-kon* OE002 is a compound based on Polyphenylene Sulfide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP .. |
|||
Tensile Strength, Yield | 125 MPa | 18200 psi | ASTM D638 |
Techmer ES HiFill® PA6/6 GF/M38 HS 38% Glass/Mineral Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 38% Filler by Weight and Mineral Filler, 38% Filler by WeightAdditive: Heat StabilizerFeatures: Heat Stabili.. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP LF002 PEEK LNP* THERMOCOMP* LF002 is a compound based on Polyetheretherketone resin containing 10% Glass Fiber. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP LF003 PEEK LNP* THERMOCOMP* LF003 is a compound based on Polyetheretherketone resin containing 15% Glass Fiber. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH8006 PPE+HIPS Noryl* NH8006 resin is a 30% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve a UL94 V0 flame rating (color specific) while offering an exceptio.. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH8006 PPE+HIPS (Asia Pacific) Noryl* NH8006 resin is a 30% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve a UL94 V0 flame rating (color specific) while offering an exceptio.. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | SABIC - Japan Method |
SABIC Innovative Plastics ULTEM JD4901 PEI (Asia Pacific) |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® HX420HP PBT Medium Flow, 30% Glass filled, Polybutylene Terephthalate (PBT) resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI).. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® HX420HP PBT (Europe-Africa-Middle East) Medium Flow, 30% Glass filled, Polybutylene Terephthalate (PBT) resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI).. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermotuf PF007IX2 PA 6 (Europe-Africa-Middle East) LNP * THERMOTUF* PF007IX2 is a compound based on PA 6 resin containing Glass Fiber. Added features include: High Impact.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | ASTM D638 |
Solvay TECHNYL® 2412GM05-D PA66, 38% glass fiber, DRY Description: Polyamid 66, reinforced with 38% of glass fiber and mineral filler, for injection molding.Available in: Asia PacificProduct Applications: TECHNYL® 2412GM05-D is used in all sectors o.. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | ASTM-D638 |
Polyram Polytron P40B01 Homopolymer Polypropylene, Chemically Coupled 40% LGF A chemically coupled 40% LGF reinforced black PP, heat stabilized for high temperature applications such as under the hood automotive parts.Information provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | ASTM D638 |
E-Polymers TEKAMID® TB120G15 , 15% Glass Fiber Reinforced PA6, DAM 15% Glass Fiber reinforced, Good surface Information provided by E-Polymers Co. Ltd. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | ASTM D638 |
Beijing Ranger Chem PBT 403 G-M50 Heat Resistant and Environmental Protection Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® B3GM35 BK 30564 15/25% Glass/Mineral Filled PA6 (Dry) Description: 25% mineral-filled and 15% glass-fiber reinforced injection-molding grade for industrial articles having medium rigidity and high dimensional stability, used e.g. for covers and handles.. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP KF006 POM (Europe-Africa-Middle East) LNP* THERMOCOMP* KF006 is a compound based on Acetal Copolymer resin containing Glass Fiber |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Verton RV004ESV_GY7E070 PA 66 Preliminary data for 20% long glass fiber filled, single pellet color gray, PA66This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 125 MPa | 18100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® VX4930 PBT (Europe-Africa-Middle East) VALOX VX4930 is a 30% glass reinforced nucleated PBT/ASA blend with excellent mechanical properties, high dimensional stability and low density. Applications: connectors and automotive industry. |