Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 12.4 MPa | 1800 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable 3201-xx05D Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable JJF102L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | |
Resinlab® CYNERGY CA6604 Adhesive Description: The CYNERGY 6600 SERIES are modified to provide greatly reduced odor and frosting of plastics. These products are ideal for bonding dissimilar materials with excellent performance on a .. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | |
Resinlab® CYNERGY CA6605 Adhesive Description: The CYNERGY 6600 SERIES are modified to provide greatly reduced odor and frosting of plastics. These products are ideal for bonding dissimilar materials with excellent performance on a .. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | |
Resinlab® CYNERGY CA6603 Adhesive Description: The CYNERGY 6600 SERIES are modified to provide greatly reduced odor and frosting of plastics. These products are ideal for bonding dissimilar materials with excellent performance on a .. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | 50 mm/min cross speed; ASTM D638 |
DuPont™ Surlyn® 8527 Ionomer Resin, Sodium
(discontinued **) Surlyn® 8527 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neu.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | Elastic; ASTM D638 |
Multibase Multi-Flex® A 8620 TPE Thermoplastic Elastomer Features: Chemical Resistance, Good Thermal Stability, GoodOzone Resistant Forms:PelletsProcessing Method:Injection Molding Uses: Automotive Interior PartsCoverings, ProtectiveInformation provide.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | ASTM D412 |
Teknor Apex ELEXAR® EL 8730 Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | ASTM D412 |
Teknor Apex TEKRON® 4300-B88 2UV Grade Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | ASTM D412 |
Teknor Apex TEKRON® 4300-B88 UV Grade Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | 50 mm/min cross speed; ASTM D638 |
DuPont™ Surlyn® 9520 Ionomer Resin, Zinc Surlyn® 9520 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | 50 mm/min cross speed; ASTM D638 |
DuPont™ Surlyn® 9650 Ionomer Resin, Zinc Surlyn® 9650 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | 50 mm/min cross speed, ASTM D638 |
DuPont™ Surlyn® 9950 Ionomer Resin, Zinc Surlyn® 9950 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | ASTM D638 |
ExxonMobil LD 506.07 Compounding and molding resin Product Description: LD 506.07 is a high flow, LDPE homopolymer designed to provide good processability. It is suitable for use in making color concentrates and injection molded articles.Availabilit.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | ASTM D638 |
ExxonMobil LD 637.LI Molding, Extrusion and Compounding Resin Product Description: LD 637.LI is a high melt index LDPE homopolymer intended for injection molding or compounding applications requiring high flow. It is ideal for tamper-evident, tear-to-open clos.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | ASTM D638 |
ExxonMobil LL 6202.19 Injection Molding Resin Product Description: LL 6202 is a narrow molecular weight butane copolymer designed for applications that require excellent toughness. This resin offers easy processability for applications that req.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | ASTM D638 |
ExxonMobil LLDPE LL 6202.19 Linear Low Density Polyethylene Resin Product Description: LL 6202 is a narrow molecular weight butane copolymer designed for applications that require excellent toughness. This resin offers easy processability for applications that req.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | Molded property |
Dow DOWLEX™ 2045A Linear Low Density Polyethylene, Blown Film Grade DOWLEX® 2045A Polyethylene blown film extrusion resin is a premier film resin for heavy duty applications. It is utilized where improved thermal stability over a broader range of processing conditi.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | Molded property |
Dow DOWLEX™ 2056 Linear Low Density Polyethylene, Heavy Duty Film Grade DOWLEX® 2056 Polyethylene resin is a premier polymer for heavy duty blown film applications. It is a low gel, high consistency polymer. It complies with U.S. FDA Regulation 21 CFR 177.1520 (c) 3.2 .. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | Molded property |
Dow DOWLEX™ 2056A Linear Low Density Polyethylene, Heavy Duty Film Grade DOWLEX® 2056A Polyethylene is a premier polymer for heavy duty blown film applications. It is a low gel, high consistency polymer with improved thermal stability and is an outstanding choice for cr.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | |
Dow DOWLEX™ 3010 Linear Low Density Polyethylene DOWLEX® 3010 Polyethylene resin is a polyethylene polymer designed to offer high performance properties such as excellent environmental stress crack resistance, tear strength, abrasion resistance, .. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | ASTM D-638 |
Axiall 1802 Moldings & Extrusions Flexible PVC Flexible PVC compound designed for food and beverage tubing applications per CFR21 and NSF61. The compound possesses exceptional clarity.Information provided by Georgia GulfGeorgia Gulf became Axia.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | ASTM D-638 |
Axiall 6640 Moldings & Extrusions Flexible PVC Injection molding compound specifically developed for footwear applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | ASTM D-638 |
Axiall 10703 Wire & Cable Flexible PVC Non-lead stabilized general purpose jacketing compound with good low temperature properties. Recommended for a maximum service temperature of 80°C at a 15 mil wall thickness.Information provided b.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | ASTM D-638 |
Axiall 19750 Wire & Cable Flexible PVC 105°C rated insulation recommended for SPT cord applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 12.4 - 14.5 MPa | 1800 - 2100 psi | ASTM D1708 |
Technetics Group Texolon™ 8534 PTFE
(Unverified Data**) PTFE CharacteristicsChemical ResistanceThermal StabilityCryogenic PropertiesLow Coefficient of FrictionLow Surface EnergyLow Dielectric ConstantHigh Volume and Surface ResistivityFlame ResistanceApp.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | TM R050-36 |
Resinlab® EP1300 Black Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1300 Black (Formerly Lab Product W092602) is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It has a pot life of about one hour and .. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | TM R050-36 |
Resinlab® EP1300 Clear Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1300 Clear (Formerly Lab Product W092602) is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It has a pot life of about one hour and .. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | Molded property |
Dow LDPE 535I Low Density Polyethylene, Liner Grade DOW LDPE 535I resin is a barefoot general purpose liner resin with medium clarity for medium modulus packaging applications. This material complies with U.S.FDA regulation 21 CFR 177.1520(c) 2.1 for.. |
|||
Tensile Strength, Yield | 12.4 MPa | 1800 psi | TM R050-36 |
Resinlab® EP1305LV Clear Epoxy Casting Resin Resinlab™ EP1305LV Clear is a black two-part epoxy casting resin designed to give good adhesion to metals and especially PVC. It has good wetting to most surfaces and is free flowing to penetrate c.. |