DuPont™ Surlyn® 9520 Ionomer Resin, Zinc

Category Polymer , Thermoplastic , Ionomer , Ionomer, Molded
Manufacturer DuPont
Trade Name Surlyn®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont™ Surlyn® 9520 Ionomer Resin, Zinc.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Surlyn® 9520 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutralization levels for this grade are optimized to deliver low temperature toughness. The resin can be injection or blow molded, and is processable by extrusion into sheets or shapes. However, its main application is as a engineering resin modifier: It improves the toughness of nylon 6 and 6/6 resins. The resin complies with the provisions of U.S. Food and Drug Administration (FDA) Title 21 Code of Regulations 177:1330 - ionomer resins.Data provided by the manufacturer.
Physical Properties Metric English Comments
Density 0.950 g/cc
0.0343 lb/in³
ASTM D792
Melt Flow 1.1 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.1 g/10 min

@Load 4.76 lb,
Temperature 374 °F
condition E; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 60
60
ASTM D2240
Tensile Strength, Ultimate 25.5 MPa
3700 psi
ASTM D638
Tensile Strength, Yield 12.4 MPa
1800 psi
50 mm/min cross speed; ASTM D638
Elongation at Break 410 %
410 %
ASTM D638
Flexural Modulus 0.260 GPa
37.7 ksi
ASTM D790
Izod Impact, Notched 5.40 J/cm
10.1 ft-lb/in
ASTM D256
Tensile Impact Strength 1190 kJ/m²
566 ft-lb/in²
ASTM D1822S
Abrasion 290
290
NBS Index; ASTM D1630
Thermal Properties Metric English Comments
CTE, linear 150 µm/m-°C

@Temperature -20.0 - 32.0 °C
83.3 µin/in-°F

@Temperature -4.00 - 89.6 °F
ASTM D696
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
Melting Point 96.0 °C
205 °F
DTA
Deflection Temperature at 0.46 MPa (66 psi) 42.0 °C
108 °F
ASTM D648
Vicat Softening Point 74.0 °C
165 °F
Rate B, ASTM D1525-70
Brittleness Temperature -71.0 °C
-95.8 °F
ASTM D746
Flame Spread 17.8 mm/min
0.701 in/min
ASTM D635
Optical Properties Metric English Comments
Haze 26 %

@Thickness 6.40 mm
26 %

@Thickness 0.252 in
ASTM D1003A