Dow DOWLEX™ 2056 Linear Low Density Polyethylene, Heavy Duty Film Grade
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Dow Chemical |
| Trade Name | DOWLEX™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DOWLEX™ 2056 Linear Low Density Polyethylene, Heavy Duty Film Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DOWLEX® 2056 Polyethylene resin is a premier polymer for heavy duty blown film applications. It is a low gel, high consistency polymer. It complies with U.S. FDA Regulation 21 CFR 177.1520 (c) 3.2 when used unmodified and according to good manufacturing practices for food contact applications, including packing or holding food during cooking. The regulation should be consulted for complete details.Film properties below based on a film thickness of 40 µm. Data provided by Dow Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg |
1.0 g/10 min @Load 4.76 lb |
Melt flow ratio I10/I2 is 8. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 26.2 MPa | 3800 psi | Molded property |
| Film Tensile Strength at Yield, MD | 10.7 MPa | 1550 psi | |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | |
| Tensile Strength, Yield | 12.4 MPa | 1800 psi | Molded property |
| Film Elongation at Break, MD | 550 % | 550 % | |
| Film Elongation at Break, TD | 650 % | 650 % | |
| Elongation at Break | 1000 % | 1000 % | Molded value |
| Secant Modulus, MD | 0.0103 GPa | 1.49 ksi | Film value |
| Secant Modulus, TD | 0.01065 GPa | 1.545 ksi | Film value |
| Coefficient of Friction | 0.70 | 0.70 | |
| Elmendorf Tear Strength MD | 375 g | 375 g | |
| Elmendorf Tear Strength TD | 600 g | 600 g | |
| Elmendorf Tear Strength, MD | 9.40 g/micron | 239 g/mil | |
| Elmendorf Tear Strength, TD | 15.0 g/micron | 381 g/mil | |
| Dart Drop | 6.90 g/micron | 175 g/mil | |
| Film Tensile Strength at Break, MD | 57.2 MPa | 8300 psi | |
| Film Tensile Strength at Break, TD | 39.3 MPa | 5700 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 106 °C | 223 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 5.0 % | 5.0 % | |
| Gloss | 75 % | 75 % | 45° |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 232 °C | 450 °F | Film extrusion temperature |
Users viewing this material also viewed the following:
- GEHR Plastics POM-C Acetal
- SABIC Innovative Plastics Noryl GFN1430V PPE+PS
- Chase Plastics CP Pryme® NN100HSL (DAM) Nylon 66, Heat Stabilized, Internally Lubricated
- Polyram PlusTek RA301G8 Nylon 6.6 for Injection Molding, 40% Glass Fiber Reinforced, Heat Stabilized
- Dow Corning C6-265 ELASTOMER
- DuPont Teijin Films Melinex® ST339 Polyester Film, 300 Gauge
- DuPont Teijin Films Mylar® A Polyester Film, 75 Gauge
- Braskem PH 0952 HOMO Polypropylene Homopolymer
- Arlon R34020W062 0.062" (1.57 mm) Uncured, Unsupported Silicone Rubber on a Kodacel Carrier
Copyright © lookpolymers.com All Rights Reserved