- Dow DOWLEX™ 2056A Linear Low Density Polyethylene, Heavy Duty Film Grade
Dow DOWLEX™ 2056A Linear Low Density Polyethylene, Heavy Duty Film Grade
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Dow Chemical |
| Trade Name | DOWLEX™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DOWLEX™ 2056A Linear Low Density Polyethylene, Heavy Duty Film Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DOWLEX® 2056A Polyethylene is a premier polymer for heavy duty blown film applications. It is a low gel, high consistency polymer with improved thermal stability and is an outstanding choice for critical film applications. It complies with U.S. FDA Regulation 21 CFR 177.1520 (c) 3.2 when used unmodified and according to good manufacturing practices for food contact applications, including packing or holding food during cooking. The regulation should be consulted for complete details.Film properties below based on a film thickness of 30 µm. Data provided by Dow Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg |
1.0 g/10 min @Load 4.76 lb |
Melt flow ratio I10/I2 is 8. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 26.2 MPa | 3800 psi | Molded property |
| Film Tensile Strength at Yield, MD | 10.7 MPa | 1550 psi | |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | |
| Tensile Strength, Yield | 12.4 MPa | 1800 psi | Molded property |
| Film Elongation at Break, MD | 550 % | 550 % | |
| Film Elongation at Break, TD | 650 % | 650 % | |
| Elongation at Break | 1000 % | 1000 % | Molded value |
| Secant Modulus, MD | 0.0103 GPa | 1.49 ksi | Film value |
| Secant Modulus, TD | 0.01065 GPa | 1.545 ksi | Film value |
| Elmendorf Tear Strength MD | 375 g | 375 g | |
| Elmendorf Tear Strength TD | 600 g | 600 g | |
| Elmendorf Tear Strength, MD | 12.5 g/micron | 318 g/mil | |
| Elmendorf Tear Strength, TD | 20.0 g/micron | 508 g/mil | |
| Dart Drop | 9.20 g/micron | 234 g/mil | |
| Film Tensile Strength at Break, MD | 57.2 MPa | 8300 psi | |
| Film Tensile Strength at Break, TD | 39.3 MPa | 5700 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 106 °C | 223 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 5.0 % | 5.0 % | |
| Gloss | 75 % | 75 % | 45° |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 232 °C | 450 °F | Film extrusion temperature |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 2010 X Natural 20% Filler Content Polypropylene
- MV Labs NA100 NaC2H3O2·3H2O Sodium acetate trihydrate
- Osprey Metals 85/15 Cu Sn Powder (Grade 80% - 22)
- Americas Styrenics Styron® 663 Polystyrene (discontinued **)
- Pyrotek Pyrocast ZG Refractory Shapes
- Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F)
- Teknor Apex APEX® 536 Polyvinyl Chloride, Flexible
- Teknor Apex Monprene® MP 1037FL Thermoplastic Elastomer
- Styron DL 396 Carboxylated SB
- SABIC Innovative Plastics NORYL FM3020V PPE+PS (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved