Polymer Property : Film Tensile Strength at Break, MD = 34.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
NOVA Chemicals Novapol® 5% LF-0718-A in PF-0118-B LDPE Film Resin Improves gloss and reduces haze in blends with LLDPE, Improves melt strength and increases output in blends with LLDPEApplications: Blends with LLDPEAdditives: Base resinFilm properties are typical ..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
NOVA Chemicals Novapol® LF-0718-A LDPE Film Resin Improves gloss and reduces haze in blends with LLDPE, Improves melt strength and increases output in blends with LLDPEApplications: Blends with LLDPEAdditives: Base resinFilm properties are typical ..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
NOVA Chemicals Sclair® 14G Butene LMDPE Film Resin Film Properties. Features: Low gel, good opacity, easy processability.Applications: Overwrap film.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D 882
NOVA Chemicals Surpass® FPs225-A Octene Copolymer sLLDPE Film Resin FPs225-A complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food, without ..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi
Reliance Industries LLDPE film - Zeolite based film Information provided by Reliance Industries
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ISO 527-3
Polimeri Europa Greenflex® FD 53 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion Greenflex FD 53 is an ethylene vinyl acetate copolymer (EVA), containing antiblocking agent, for blown film extrusion. Films produced with Greenflex FD 53 exhibit good sealing properties, high flex..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
DuPont™ Sclairfilm® SL-3 LLDPE Film, Laminating, 76.2 µm Thickness (discontinued **) Data provided by DuPont Packaging Polymers.SL is a linear low density polyolefin film which offers a combination of toughness and durability plus outstanding clarity. These have superior tensile st..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
Eastman 1830F Polyethylene (discontinued **) Polyethylene 1830F is a low-density formulation with no slip or antiblock. It is suggested for film applications requiring high clarity, good tear and impact strength, a wide heat sealing range and..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
Eastman E6838-922F Polyethylene (discontinued **) E6838-922F is a low density formulation with medium slip and medium antiblock. Outstanding optical properties make this material an excellent choice for food packaging applications.List of Applicat..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
NOVA Chemicals Sclair® 10A Octene VLDPE Film Resin (discontinued **) Film Properties. Features: Low gel, excellent sealability, easy processability, excellent clarity.Applications: Blending resin for improved toughness.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
NOVA Chemicals Novapol® PF-0118-B Butene LLDPE Film Resin Film Properties. Features: Toughness and strength.Applications: Trash bags, liners, general packaging.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
NOVA Chemicals Novapol® PF-0118-C Butene LLDPE Film Resin Film Properties. Features: Toughness and strength.Applications: Industrial liners, heavy duty bags.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
NOVA Chemicals Novapol® PF-0118-D Butene LLDPE Film Resin Film Properties. Features: Toughness and strength, thin films.Applications: Trash bags, garment film, bags-on-roll.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
NOVA Chemicals Novapol® PF-0118-F Butene LLDPE Film Resin Film Properties. Features: Toughness and strength.Applications: Stretch wrap, blend resin, industrial packaging.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
ExxonMobil Escorene® LD-708 EVA Film Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.A 15.5% vinyl acetate copolymer film resin. Film made from LD-708 exhibits good impact strength and superior heat sealability.Applications: Primal ..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
NOVA Chemicals Sclair® 14L1 Octene LMDPE Film Resin (discontinued **) Low gel, Good clarity, Excellent sealing characteristicsApplications: Lamination, Co-extrusionAdditives: Process stabilizer, polymer process aidFilm properties are typical of blown film extruded at ..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	2 in per min; ASTM D882
Chevron Phillips MarFlex® D139 m-LLDPE Linear Low Density Polyethylene Low Density PolyethyleneCustomer Benefits: Possesses the typical physical properties of metallocene polyethylenes with the added potential benefit of improved processability (bubble stability, down-..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	2 in per min; ASTM D882
Chevron Phillips MarFlex® D143 m-LLDPE Linear Low Density Polyethylene Low Density PolyethyleneCustomer Benefits: This metallocene LLDPE film resin possesses the typical physical properties of metallocene polyethylenes with the added potential benefit of improved proce..
Film Tensile Strength at Break, MD	34.0 MPa @Thickness 0.0250 mm	4930 psi @Thickness 0.000984 in	ASTM D882
Equate EFDA-7047 LLDPE Film Extrusion Resin EFDA-7047 is a linear low-density polyethylene resin for tubular blown film extrusion. Films made from this resin have good toughness, high tensile strength and puncture resistance. EFDA-7047 does n..
Film Tensile Strength at Break, MD	34.0 MPa @Thickness 0.0250 mm	4930 psi @Thickness 0.000984 in	ASTM D882
Equate EFDC-7087 LLDPE Film Extrusion Resin EFDC-7087 is a linear low-density polyethylene resin for tubular blown film extrusion. Films made from EFDC-7087 have good toughness, high tensile strength and outstanding puncture resistance. EFDC-..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
Braskem EB 861 LDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Coextruded films; Shrink films for pallets; general purpose; mulching films. Information p..
Film Tensile Strength at Break, MD	34.0 - 50.0 MPa	4930 - 7250 psi	Average value: 40.4 MPa Grade Count:20
Overview of materials for Linear Medium Density Polyethylene (LMDPE), Film This property data is a summary of similar materials in the MatWeb database for the category "Linear Medium Density Polyethylene (LMDPE), Film". Each property range of values reported is minimum and..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
ExxonMobil Escorene® LD-331 EVA Film Resin, Very High Clarity, Very High Impact (discontinued **) Data provided by the manufacturer, Exxon Chemical.A 5.8% vinyl acetate copolymer, high clarity film resin. Film made from this resin exhibits superior impact strength and heat sealability.Applicati..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
Chevron Phillips 7105DKT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **) Resin Type: Hexene Copolymer, High Antiblock, Processing Aid Version of 7105T, Cast/Blown Film ResinCharacteristics: Good Stiffness at Thin Gauges, Good Drawdown, Can be used straight or blended wit..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
DuPont™ Sclairfilm® SL-1 LLDPE Film, Laminating, 50.8 µm Thickness (discontinued **) Data provided by DuPont Packaging Polymers.SL is a linear low density polyolefin film which offers a combination of toughness and durability plus outstanding clarity. These have superior tensile st..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
DuPont™ Sclairfilm® SL-1 LLDPE Film, Laminating, 76.2 µm Thickness (discontinued **) Data provided by DuPont Packaging Polymers.SL is a linear low density polyolefin film which offers a combination of toughness and durability plus outstanding clarity. These have superior tensile st..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
DuPont™ Sclairfilm® SL-3 LLDPE Film, Laminating, 38.1 µm Thickness (discontinued **) Data provided by DuPont Packaging Polymers.SL is a linear low density polyolefin film which offers a combination of toughness and durability plus outstanding clarity. These have superior tensile st..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
NOVA Chemicals Sclair® 11B4 Octene LLDPE Film Resin (discontinued **) Film Properties. Features: Low gel, excellent seal characteristics, easy processability.Applications: Specialty lamination, co-extrusion.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
DuPont™ Sclairfilm® SL-1 LLDPE Film, Laminating, 38.1 µm Thickness (discontinued **) Data provided by DuPont Packaging Polymers.SL is a linear low density polyolefin film which offers a combination of toughness and durability plus outstanding clarity. These have superior tensile st..
Film Tensile Strength at Break, MD	34.0 MPa	4930 psi	ASTM D882
DuPont™ Sclairfilm® SL-3 LLDPE Film, Laminating, 50.8 µm Thickness (discontinued **) Data provided by DuPont Packaging Polymers.SL is a linear low density polyolefin film which offers a combination of toughness and durability plus outstanding clarity. These have superior tensile st..