- NOVA Chemicals Sclair® 11B4 Octene LLDPE Film Resin (discontinued **)
NOVA Chemicals Sclair® 11B4 Octene LLDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 11B4 Octene LLDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Low gel, excellent seal characteristics, easy processability.Applications: Specialty lamination, co-extrusion.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D792 |
| Melt Flow | 0.77 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.77 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 58 | 58 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 730 % | 730 % | ASTM D882 |
| Secant Modulus, MD | 0.208 GPa | 30.2 ksi | ASTM D882 |
| Secant Modulus, TD | 0.207 GPa | 30.0 ksi | ASTM D882 |
| Coefficient of Friction | 0.20 | 0.20 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 12.0 g/micron | 305 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 21.0 g/micron | 533 g/mil | ASTM D1922 |
| Dart Drop | 6.00 g/micron | 152 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 34.0 MPa | 4930 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 220 °C | 410 - 428 °F |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8711 (UF) Synthetic Oil
- Plenco 7000 Black General Purpose Woodflour Filled Phenolic Molding Compound (discontinued **)
- Less Common Metals Neodymium Sublimed Rare Earth Metal
- GRECO ISOTHANE 1075A Poly(adipate)ester TPUÂ Resin
- A. Schulman POLYFLAM™ E-17338 22% CACO3 Filled Copolymer Polypropylene
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.0 PHR Thanecure® ZM
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR Mistron Vapor Filler
- ConocoPhillips Syncon® EP Gear Oil, AGMA number 8EP
- ExxonMobil Oppalyte™ 35HM247 OPP Film
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 288°C Temper
Copyright © lookpolymers.com All Rights Reserved