NOVA Chemicals Novapol® PF-0118-F Butene LLDPE Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film |
| Manufacturer | NOVA Chemicals |
| Trade Name | Novapol® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Novapol® PF-0118-F Butene LLDPE Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Toughness and strength.Applications: Stretch wrap, blend resin, industrial packaging.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 760 % | 760 % | ASTM D882 |
| Secant Modulus, MD | 0.180 GPa | 26.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.60 | >= 0.60 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 3.90 g/micron | 99.1 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 11.8 g/micron | 300 g/mil | ASTM D1922 |
| Dart Drop | 3.70 g/micron | 94.0 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 34.0 MPa | 4930 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 26.0 MPa | 3770 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 12 % @Thickness 0.0250 mm |
12 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 55 % | 55 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 195 - 220 °C | 383 - 428 °F |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE G 7680 NAT
- RheTech Products P254-00 Polypropylene Copolymer, Natural
- MMCC Cu/Al2O3 Particulate Copper Matrix Composite
- Industeel URANUS® 52N+ 25 Cr Super Duplex Stainless Steel with PREN = 40
- Lanxess Durethan® BG 30 X 000000 Nylon 6, 30% Glass Fiber
- Techmer ES Electrablend® ABS CF30 BK 30% Carbon Filled
- Williams Advanced Alloys Wambraze™ WB705 Solder
- Braskem GV0350 HDPE Blow Molding Polyethylene Copolymer
- BACT Dylyn® Diamond-Like Nanocomposite Coating
- Beijing Ranger Chem SM-602RX70 Solvent Based Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved