Equate EFDC-7087 LLDPE Film Extrusion Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer Equate
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Equate EFDC-7087 LLDPE Film Extrusion Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EFDC-7087 is a linear low-density polyethylene resin for tubular blown film extrusion. Films made from EFDC-7087 have good toughness, high tensile strength and outstanding puncture resistance. EFDC-7087 contains high levels of slip and antiblocking agent. The product offers excellent draw down capability for thinner gauge film production. The films have good seal-ability and machinability for easy conversion on high-speed machinesApplications: EFDC-7087 is recommended for the manufacture of thin gauge liner films, garment bags and other industrial and consumer packaging applications requiring toughness and puncture resistanceInformation provided by Equate
Physical Properties Metric English Comments
Bulk Density 0.530 g/cc
0.0191 lb/in³
ASTM D1895
Density 0.918 g/cc
0.0332 lb/in³
ASTM D792
Thickness 25.0 microns
0.984 mil
As Tested
Melt Flow 1.0 g/10 min

@Load 2.16 kg
1.0 g/10 min

@Load 4.76 lb
ASTM D1238
Mechanical Properties Metric English Comments
Elmendorf Tear Strength, MD 35.0 g/micron

@Thickness 0.0250 mm
889 g/mil

@Thickness 0.000984 in
ASTM D1922
Elmendorf Tear Strength, TD 135 g/micron

@Thickness 0.0250 mm
3430 g/mil

@Thickness 0.000984 in
ASTM D1922
Dart Drop 4.20 g/micron

@Thickness 0.0250 mm
107 g/mil

@Thickness 0.000984 in
ASTM D1709 A
Dart Drop Test 105 g
0.232 lb
F50; ASTM D1709 A
Film Tensile Strength at Break, MD 34.0 MPa

@Thickness 0.0250 mm
4930 psi

@Thickness 0.000984 in
ASTM D882
Film Tensile Strength at Break, TD 26.0 MPa

@Thickness 0.0250 mm
3770 psi

@Thickness 0.000984 in
ASTM D882
1% Secant Modulus, MD 193 MPa

@Thickness 0.0250 mm
28000 psi

@Thickness 0.000984 in
ASTM D882
1% Secant Modulus, TD 221 MPa

@Thickness 0.0250 mm
32100 psi

@Thickness 0.000984 in
ASTM D882
Thermal Properties Metric English Comments
Melting Point 124 °C
255 °F
Equate Test Method
Optical Properties Metric English Comments
Haze 14 %
14 %
ASTM D1003
Gloss 55 %
55 %
45°; ASTM D2457
Processing Properties Metric English Comments
Zone 1 175 °C
347 °F
Zone 2 185 °C
365 °F
Zone 3 190 °C
374 °F
Zone 4 185 °C
365 °F
Adapter Temperature 185 °C
365 °F
Die Temperature 185 °C
365 °F
Head Temperature 185 °C
365 °F
Die Opening >= 0.180 cm
>= 0.0709 in
Blow-up Ratio (BUR) 2.0
2.0
2:1 As Tested
Descriptive Properties Value Comments
Puncture Energy 70 J/mm
Equate Test Method