NOVA Chemicals Sclair® 14G Butene LMDPE Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Linear Medium Density Polyethylene (LMDPE), Film |
| Manufacturer | NOVA Chemicals |
| Trade Name | Sclair® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 14G Butene LMDPE Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Low gel, good opacity, easy processability.Applications: Overwrap film.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in³ | ASTM D792 |
| Moisture Vapor Transmission | 0.230 cc-mm/m²-24hr-atm | 0.584 cc-mil/100 in²-24hr-atm | ASTM D1434 |
| Water Vapor Transmission | 5.20 g/m²/day | 0.335 g/100 in²/day | |
| 9.00 g/m²/day | 0.580 g/100 in²/day | ASTM D1434 | |
| Oxygen Transmission | 78.0 cc-mm/m²-24hr-atm | 198 cc-mil/100 in²-24hr-atm | or 3100 cc/m²-atm-24 hr per 25 µm film; 38°C; 90% RH Difference |
| Oxygen Transmission Rate | 2300 cc/m²/day | 148 cc/100 in²/day | ASTM D1434 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 0.72 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.72 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 17.0 MPa | 2470 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 17.0 MPa | 2470 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 900 % | 900 % | ASTM D882 |
| Secant Modulus, MD | 0.390 GPa | 56.6 ksi | ASTM D882 |
| Secant Modulus, TD | 0.520 GPa | 75.4 ksi | ASTM D882 |
| Coefficient of Friction | 0.24 | 0.24 | ASTM D1894 |
| >= 0.40 | >= 0.40 | ASTM D1894 | |
| Elmendorf Tear Strength, MD | 1.05 g/micron | 26.7 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 3.42 g/micron | 86.9 g/mil | ASTM D1922 |
| Dart Drop | 1.63 g/micron | 41.4 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 34.0 MPa | 4930 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 39.0 MPa | 5660 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 20 % @Thickness 0.0250 mm |
20 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 48 % | 48 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 220 °C | 410 - 428 °F |
Users viewing this material also viewed the following:
- Nyco 10 AS WOLLASTOCOAT® Wollastonite
- Global MM-1018 Low Density Polyethylene, Lamination Coating Grade (discontinued **)
- SABIC Innovative Plastics NORYL GTX GTX678 PPE+PA (Asia Pacific)
- SABIC Innovative Plastics NORYL GTX GTX918W PPE+PS+PA (Asia Pacific)
- A. Schulman POLYFORT™ FPP 1080 Glass Fiber-Reinforced Homopolymer Polypropylene
- ELASTO UK Dryflex® 502900S SEBS Based Material, Unfilled Qualities, 90A Hardness, Black
- Cytec (Conap) RN-1210 / EA-028 Conapoxy® Resin / Conacure® Hardener
- SABIC Innovative Plastics XYLEX X7519HP PC+POLYESTER (Europe-Africa-Middle East)
- Total Finathene® CD 481 HDPE conduit (discontinued **)
Copyright © lookpolymers.com All Rights Reserved