Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 345 MPa @Thickness 15.9 - 152 mm |
50000 psi @Thickness 0.625 - 6.00 in |
|
Niagara LaSalle CPO® Cold Finished Steel Bar CPO® chrome plated steel bars and tubes are manufactured to meet the specific needs for piston rod material in hydraulic and pneumatic cylinders. They are readily available in standard and custom s.. |
|||
Tensile Strength, Yield | 345 MPa @Thickness 15.9 - 152 mm |
50000 psi @Thickness 0.625 - 6.00 in |
|
Niagara LaSalle IHCP® Cold Finished Steel Bar IHCP® steel bars and tubes are manufactured to meet the specific needs for piston rod material in hydraulic and pneumatic cylinders. They are readily available in standard and custom sizes, chemist.. |
|||
Tensile Strength, Yield | 345 MPa @Temperature 177 °C |
50000 psi @Temperature 350 °F |
0° Direction, Dry; ASTM D638 |
Park Electrochemical Nelcote® E-720 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-720 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-720 has a proven history in many demanding aerospac.. |
|||
Tensile Strength, Yield | 345 MPa @Temperature 138 °C |
50000 psi @Temperature 280 °F |
0° Direction, Dry, Autoclave; ASTM D638 |
Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-746 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-746 has a proven history in many demanding aerospac.. |
|||
Tensile Strength, Yield | 345 MPa @Temperature 21.1 °C |
50000 psi @Temperature 70.0 °F |
0° Direction, Wet; ASTM D638 |
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 120 E-Glass Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle.. |
|||
Tensile Strength, Yield | 345 MPa @Temperature 82.2 °C |
50000 psi @Temperature 180 °F |
0° Direction, Wet; Vacuum/Oven Cured; ASTM D3039-95 |
Park Electrochemical Nelcote® E-765 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-765 is a tough 250°F cure prepreg system designed to replace 350°F cure systems in aircraft structural applications. FAA-approved Design Allowable Databases are available upon request... |
|||
Tensile Strength, Yield | 345 MPa @Thickness 19.0 mm, Temperature 538 °C |
50000 psi @Thickness 0.750 in, Temperature 1000 °F |
0.2% offset |
Haynes Ultimet® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Tensile Strength, Yield | 345 MPa @Thickness 12.7 mm, Temperature 20.0 °C |
50000 psi @Thickness 0.500 in, Temperature 68.0 °F |
0.2% offset |
Haynes Hastelloy® C-2000® alloy, flat products Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
Tensile Strength, Yield | 345 - 655 MPa @Strain 0.200 %, Thickness <=25.4 mm |
50000 - 95000 psi @Strain 0.200 %, Thickness <=1.00 in |
Cold Drawn Bars |
Schmolz + Bickenbach UGIMA® 316/316L Stainless Steel Bar Description: 316/316L UGIMA® is Ugitech’s improved machining grade produced only by Ugitech. It is identical in every way to regular 316L, except with respect to machinability. 316/316L UGIM.. |
|||
Tensile Strength, Yield | >= 345 MPa @Thickness 16.0 - 50.0 mm |
>= 50000 psi @Thickness 0.630 - 1.97 in |
|
ThyssenKrupp COR-TEN B Structural Steel This Material Specification applies to plates up to 50 mm in thickness made from COR-TEN B.Definition: Weathering means that due to its chemical composition the COR-TEN B steel, when utilized unprot.. |
|||
Tensile Strength, Yield | 345 MPa @Strain 0.200 %, Thickness 203 - 305 mm |
50000 psi @Strain 0.200 %, Thickness 8.00 - 12.0 in |
Tension |
Crucible Steel Aquamet® 18 Stainless Steel AQUAMET 18 is an austenitic stainless steel with corrosion resistance comparable to that of Type 304. Its good strength and toughness make it an ideal shafting material for workboats. It provides a .. |
|||
Tensile Strength, Yield | 345 MPa @Strain 0.200 %, Thickness 76.2 - 305 mm |
50000 psi @Strain 0.200 %, Thickness 3.00 - 12.0 in |
Tension |
Crucible Steel Aquamet® 19 Stainless Steel AQUAMET 19 is a modified Type 304 stainless steel that is fully austenitic and non-magnetic. Strengthened by adding nitrogen to the melt, it has better corrosion resistance than Type 304 stainless. .. |
|||
Tensile Strength, Yield | >= 345 MPa @Strain 0.500 %, Thickness >=25.4 mm |
>= 50000 psi @Strain 0.500 %, Thickness >=1.00 in |
|
Cadi 150 Copper Alloy A small addition of Zr to copper improves resistance to softening and resists deformation at high temperatures where normal copper would soften rapidly. Zirconium copper is used as a Class 1 electr.. |
|||
Tensile Strength, Yield | >= 345 MPa @Strain 0.500 %, Thickness >=25.4 mm |
>= 50000 psi @Strain 0.500 %, Thickness >=1.00 in |
|
Cadi 162 Copper Alloy Cadmium addition to copper increases hardness and resistance to softening. C16200 is utilized in numerous applications where fatigue strength and high electrical conductivity are required. Cadmium.. |
|||
Tensile Strength, Yield | >= 345 MPa @Strain 0.200 % |
>= 50000 psi @Strain 0.200 % |
|
Carlson Nitronic® 60® Austenitic Stainless Steel General DescriptionNitronic 60 is an anti-galling and wear resistant austenitic stainless steel. It provides a significantly lower cost alternative to combat wear and galling when compared with cob.. |
|||
Tensile Strength, Yield | 345 MPa @Strain 0.200 % |
50000 psi @Strain 0.200 % |
Typical for Plate, Annealed, 0.875" |
AK Steel NITRONIC® 30 Austenitic Stainless Steel AK Steel NITRONIC 30 Stainless Steel offers significantly higher strength than Type 304 and potential for applications requiring good resistance to aqueous and atmospheric corrosion resistance combi.. |
|||
Tensile Strength, Yield | 345 MPa @Temperature 100 °C |
50000 psi @Temperature 212 °F |
|
ATI Allegheny Ludlum AL 4565™ Corrosion Resistant Stainless Steel Characteristics:Very high resistance to pitting and crevice corrosion Excellent general corrosion resistance in a variety of media Higher mechanical propertied then conventional stainless steels Go.. |
|||
Tensile Strength, Yield | 345 MPa @Diameter 19.1 mm, Temperature 25.0 °C |
50000 psi @Diameter 0.752 in, Temperature 77.0 °F |
0.2% offset |
Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |