Cadi 150 Copper Alloy

Category	Metal , Nonferrous Metal , Copper Alloy
Manufacturer	Cadi Company
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Cadi 150 Copper Alloy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

A small addition of Zr to copper improves resistance to softening and resists deformation at high temperatures where normal copper would soften rapidly. Zirconium copper is used as a Class 1 electrode material to minimize sticking when resistance spot welding galvanized materials.Forms: RodBarInformation provided by Cadi Company.

Physical Properties	Metric	English	Comments
Density	8.89 g/cc	0.321 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell B	55 @Diameter 50.8 - 76.2 mm	55 @Diameter 2.00 - 3.00 in
	60 @Diameter 25.4 - 50.8 mm	60 @Diameter 1.00 - 2.00 in
	>= 65 @Diameter <=25.4 mm	>= 65 @Diameter <=1.00 in	hard temper
Tensile Strength at Break	>= 345 MPa @Thickness >=25.4 mm	>= 50000 psi @Thickness >=1.00 in
	>= 414 MPa @Thickness <=25.4 mm	>= 60000 psi @Thickness <=1.00 in
Tensile Strength, Yield	>= 345 MPa @Strain 0.500 %, Thickness >=25.4 mm	>= 50000 psi @Strain 0.500 %, Thickness >=1.00 in
	>= 414 MPa @Strain 0.500 %, Thickness <=25.4 mm	>= 60000 psi @Strain 0.500 %, Thickness <=1.00 in
Modulus of Elasticity	117 GPa	17000 ksi

Thermal Properties	Metric	English
Thermal Conductivity	366.6 W/m-K	2544 BTU-in/hr-ft²-°F
Melting Point	980.0 - 1080 °C	1796 - 1976 °F
Solidus	980.0 °C	1796 °F
Liquidus	1080 °C	1976 °F

Component Elements Properties	Metric	English	Comments
Copper, Cu	99.85 %	99.85 %
Zirconium, Zr	0.15 %	0.15 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	<= 0.00000216 ohm-cm	<= 0.00000216 ohm-cm	Calculated from Min 80 %IACS, up to 3" diameter/any thickness

Processing Properties	Metric	English	Comments
Processing Temperature	649 °C	1200 °F	Brazing, <15 minutes

Descriptive Properties	Value	Comments
RMWA Class	1