| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON QD000I PA 6/10.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* QD000I is a compound based on Nylon 6/10 resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.280 % | 0.280 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | 52.7 % | 52.7 % | ASTM D638 |
| Flexural Strength | 54.0 MPa | 7830 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 249 ksi | ASTM D790 |
| Izod Impact, Notched | 6.03 J/cm | 11.3 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 117 µm/m-°C @Temperature -40.0 - 40.0 °C |
65.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 117 µm/m-°C @Temperature -40.0 - 40.0 °C |
65.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C @Thickness 3.20 mm |
131 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D257 |
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Resin Technology Group 1105 Oxy-Bond™ Two-Component Epoxy Adhesive
- Chevron Phillips HiD® 9410 HDPE Blow Molding Resin (discontinued **)
- Cookson Group Plaskon® SMT-B-1FX (146.801) Epoxy Molding Compound for PBGAs (discontinued **)
- GRECO ISOTHANE 1680AE Polyether TPU Resin
- Momentive Performance Materials Siloprenâ„¢ LSR 3186/50 Liquid Silicone Rubber - Self-Lubricating / Low Compression Set
- Heatbath/Park Sta-Hard 45 Neutral Salt
- SABIC Innovative Plastics Valox® 176HP PBT
- A. Schulman POLYBATCH™ Weatherwood 60190U Concentrate Based In LLDPE
- 3M Scotchkote™ 60EG 533 Urethane Elastomer
- Arkema Group Evatane® 1005 VN 4 Ethylene Vinyl Acetate
Copyright © lookpolymers.com All Rights Reserved