- Polymer Property : Tensile Strength at Break = 4060 psi
Polymer Property : Tensile Strength at Break = 4060 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 28.0 MPa | <= 4060 psi | ISO/R527 |
| Polykemi AB POLYfill PPH K20020 D Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| Eastman Eastar GN002 Copolyester, Natural
(discontinued **) Eastar GN002 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN002 copolyester will not crystallize and thus offers wider processing latitude tha.. |
|||
| Tensile Strength at Break | <= 28.0 MPa | <= 4060 psi | ISO/R527 |
| Polykemi AB POLYfill PP HIP8040F VT2 Polypropylene, Mineral Reinforced, Heat Resistant Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D4895 |
| 3M Dyneon™ TF 2071 PTFE
(discontinued **) Processable by standard paste extrusion methodTF 2071 and TF 2072 have a wide processing range because of high maximum allowable reduction ratioTF 2071 is recommended for high quality tubing and wir.. |
|||
| Tensile Strength at Break | 28.0 - 35.0 MPa | 4060 - 5080 psi | ASTM D638 |
| Manifattura Cattaneo PTFE Polytetrafluoroethylene Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ISO 37 |
| Huntsman AVALON® 90 AHT DP Thermoplastic Polyurethane Performance Features: AVALON® injection molding products are trusted worldwide to deliver:Outstanding flex performanceExcellent slip resistancePerfect surface definitionTransparency and transluce.. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | UL 1581 |
| SABIC Innovative Plastics NORYL WCA871 PPE-TPE (Asia Pacific) Halogen-free flame retardant Flexible Noryl extrusion grade intended for evaluation in applications such as insulation and cable jacket. Flame retardant performance and mechanical properties capable.. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL WCV063 PPE+SEBS+Polyolefin Flexible, non-halogenated FR, mPPE extrusion grade material for evaluation in automotive wire coating applications requiring ISO6722. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL WCV063 PPE+SEBS+Polyolefin (Asia Pacific) Flexible, non-halogenated FR, mPPE extrusion grade material for evaluation in automotive wire coating applications requiring ISO6722. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP ML003S PP LNP* LUBRICOMP* ML003S is a compound based on Polypropylene resin containing 15% PTFE. Added features include: Heat Stabilized, Wear Resistant. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-LOY A3000T ABS (Europe-Africa-Middle East) LNP* Stat-loy* A3000T is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: Antistat. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL PPX PPX7200 PPE+PP+PS (Europe-Africa-Middle East) PP+PPE+PS. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61-capable. UL-94 HB listed. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | 50 mm/min; ASTM D638 |
| SK Chemicals SKYGREEN® PETG 2008 Specially Formulated PET Copolymer Resin SKYGREEN PETG is an amorphous copolyester in which a certain amount of ethylene glycol is replaced with 1,4-cyclohexane dimethanol (CHDM), which prevent crystallization, leading to improved processa.. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | 50 mm/min; ISO 527 |
| Chi Mei Polylac® PA-765A ABS - Flame Retardant F.R. High Flow |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | 50mm/min; ISO 527-2 |
| Denka TE-30 Transparent Resin Polymer (MABS resin) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| Aclo Accutech Polypropylene Copolymer HP0334W10L Wollastonite Reinforced |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0336T20L1 Talc Reinforced |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D412 |
| Alliance Polymers Zythane™ 6075A Thermoplastic Polyurethane Elastomer Zythane™ 6075A is a polycaprolactone-based TPU specifically formulated for injection molding applications .It exhibits excellent low compression set, abrasion resistance and toughness and has good .. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | |
| AorTech Biomaterials Elast-Eon™ E2-945 Biomedical Polyurethane Pellets Elast-Eon™ polymers are used in biomedical applications. They have high biostability so they can be used for long term implantation. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| 3M Dyneon™ FEP 6303Z Fluorinated Ethylene Propylene Fluorothermoplastic Granules Dyneon FEP 6303Z is offered for extrusion, injection molding and transfer molding for the wire and cable and chemical process industries. Their distinguishing features include: Excellent electrical .. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| Aclo Accutech Polypropylene Copolymer CP0436G10M20CL Glass/Mineral Reinforced Coupled |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| Aclo Accutech Polypropylene Copolymer HP0335W40L Wollastonite Reinforced |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0339M30L Mica Reinforced |
|||
| Tensile Strength at Break | <= 28.0 MPa | <= 4060 psi | ISO/R527 |
| Polykemi AB POLYfill PPH TS3020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Tensile Strength at Break | <= 28.0 MPa | <= 4060 psi | ISO/R527 |
| Polykemi AB POLYfill PPH TS8020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ISO 527-2 |
| Total Lacqrene® 852 High Impact Polystyrene
(discontinued **) LACQRENE® 852 is a flame retardant, high impact polystyrene, halogen free, with excellent thermal stability.ApplicationCopier, Fax, Printers, Television, decoders, Hi-FiInformation provided provide.. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycolac® EX39 ABS Highest impact extrusion ABS for sheet and blow molding applications. |
|||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 15T1040 PP SABIC® PPcompound 15T1040 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound, suitable for injection molding applications. The IMDS ID is 16487994 |
|||
| Tensile Strength at Break | <= 28.0 MPa | <= 4060 psi | ISO/R527 |
| Polykemi AB POLYfill PPH TS2040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||