Total Lacqrene® 852 High Impact Polystyrene (discontinued **)

Category	Polymer , Thermoplastic , Polystyrene (PS)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total Lacqrene® 852 High Impact Polystyrene (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LACQRENE® 852 is a flame retardant, high impact polystyrene, halogen free, with excellent thermal stability.ApplicationCopier, Fax, Printers, Television, decoders, Hi-FiInformation provided provided by Total Petrochemicals.Total Petrochemicals includes former Fina and Atofina plastics product lines.

Physical Properties	Metric	English	Comments
Density	1.06 g/cc	0.0383 lb/in³	ISO 1183
Water Absorption	<= 0.10 %	<= 0.10 %	ISO 62
Linear Mold Shrinkage	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in
Melt Flow	4.0 g/10 min @Load 5.00 kg, Temperature 200 °C	4.0 g/10 min @Load 11.0 lb, Temperature 392 °F	ISO 1133H
	12 g/10 min @Load 5.00 kg, Temperature 200 °C	12 g/10 min @Load 11.0 lb, Temperature 392 °F	ISO 1133H

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	28.0 MPa	4060 psi	ISO 527-2
Tensile Strength, Yield	32.0 MPa	4640 psi	ISO 572-2
Elongation at Break	40 %	40 %	ISO 527-2
Flexural Modulus	2.50 GPa	363 ksi	ISO 178
Izod Impact, Notched (ISO)	6.00 kJ/m²	2.86 ft-lb/in²	ISO 180/1A
Charpy Impact, Notched	0.550 J/cm²	2.62 ft-lb/in²	ISO 1791/eU

Thermal Properties	Metric	English	Comments
Vicat Softening Point	81.0 °C	178 °F	50N (T° increase = 5°C/h); ISO 306B50
	90.0 °C	194 °F	10N (T° increase = 50°C/h); ISO 306A50

Processing Properties	Metric	English	Comments
Processing Temperature	<= 270 °C	<= 518 °F