Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 26.0 MPa | <= 3770 psi | ISO/R527 |
Polykemi AB POLYelast TPE ZC100 D40 Thermoplastic Elastomer Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 26.0 MPa | <= 3770 psi | ISO/R527 |
Polykemi AB POLYfill PPC T20040 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 26.0 MPa | <= 3770 psi | ISO/R527 |
Polykemi AB POLYfill PP EIP12030RF Polypropylene/EPDM, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | 0.2 inches/minute; ASTM D 638 |
NOVA Chemicals Dylark® FG2500 High-Heat Styrenic Copolymer Product Description and Features: Styrenic copolymer with high-heat resistance, high-impact strength and good toughness. Resins used in food grade sheet extrusion and injection molding application.. |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
Petroquimica Triunfo Tritheva® TN 8093 EVA Copolymer The Tritheva TN 8093 resin is a fractional MI copolymer of Ethylene-Vinyl Acetate (EVA), developed to meet the multi-layer and blending film applications where are required high strength, with high .. |
|||
Tensile Strength at Break | 26.0 - 28.0 MPa | 3770 - 4060 psi | ASTM D683 |
Loxim 821 02T HB Polypropylene Compound, 20% Talc Filled, Flame Retardant Information provided by Loxim Industries |
|||
Tensile Strength at Break | 26.0 - 28.0 MPa | 3770 - 4060 psi | ASTM D683 |
Loxim 830 02C HB Polypropylene Compound, 30% Calcite Filled, Flame Retardant Information provided by Loxim Industries |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | |
JPJ Technologies 7800M HDPE Extrusion Information provided by JPJ Technologies |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | ISO 37 |
Huntsman AVALON® 80 AE Thermoplastic Polyurethane Performance Features: AVALON® injection molding products are trusted worldwide to deliver:Outstanding flex performanceExcellent slip resistancePerfect surface definitionTransparency and transluce.. |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | after 7days @136°C; UL 1581 |
SABIC Innovative Plastics NORYL WCA875 PPE-TPE (Europe-Africa-Middle East) Non-halogenated flame retardant Flexible Noryl extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Excellent flame retardant performance with balanced t.. |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | UL 1581 |
SABIC Innovative Plastics NORYL WCA901 PPE-TPE Non-Halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications, capable of meeting VW-1 and 105°C end use temperature requirements as defined by UL.. |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | UL 1581 |
SABIC Innovative Plastics NORYL WCA901 PPE-TPE (Europe-Africa-Middle East) Non-Halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications, capable of meeting VW-1 and 105°C end use temperature requirements as defined by UL.. |
|||
Tensile Strength at Break | >= 26.0 MPa | >= 3770 psi | ASTM D638 |
Solvay Specialty Polymers Hyflon® PFA M620 Perfluoroalkoxy (PFA) Hyflon® PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat res.. |
|||
Tensile Strength at Break | >= 26.0 MPa @Strain >=100 % |
>= 3770 psi @Strain >=100 % |
ISO R527 |
Shanghai Ofluorine 9201F PVDF Powder for cables Description: Excellent mechanical properties, heat resistance and flame resistance, PVDF for cable can bear high temperature, corrosive chemicals etc harsh working environment, which has low smoke, .. |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® X5410 PC+PET (Asia Pacific) Mineral filled PC+PET resin with high heat dimensional stability for paint systems. It has very low CTE and excellent flow - impact balance for automotive exterior applications, like body panels, ta.. |
|||
Tensile Strength at Break | >= 26.0 MPa | >= 3770 psi | |
Sibur SKS-30 ARK 1st Grade Styrene-Butadiene Rubber (SBR) SBR-1500. For use in the shoe industry and for production of vulcanized micro-porous sole rubbers and rubber technical articles. |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | ISO 527-2 |
Tisan TISOPLEN® Flame Retardant (V0). Heat Stabilized Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
Eastman Eastar MN052 Polyester, Natural Eastar polyester MN052 is a thermoplastic condensation homopolymer produced by a continuous melt-phase polymerization process followed by a solid-state polymerization process. It has been crystalliz.. |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | ISO 527 |
Eastman Spectar® 14471 Copolyester Spectar copolyester extrudes into plastic sheet that is sparkling clear, tough, chemically resistant, odor-free, versatile, easy to work with and affordable. Its toughness allows fabricators to use .. |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D 638 |
Cossa Polimeri ESTADIENE 0425 GFS Acrylonitrile Butadiene Styrene, 13% Glass Filled ABS with 13% short glass fiberExcellent mechanical and thermal propertiesInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 26.00 MPa | 3770 psi | JIS-K-6723 |
Denka VINYKON W5230 PVC, W grade for non-migratory sheath and special items A PVC resin compound offering excellent physical properties and workability. A broad product lineup is available, including hard and soft grades, as well as those for extrusion and injection molding.. |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | Film Property, 50 µm thickness; ASTM D882 |
Arkema Group OREVAC® 9304 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0334T40L Talc Reinforced |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | ISO 527 |
Breplast Bretene PP Polypropylene Composite Recovered polypropylene compositeInformation provided by Breplast S.p.A. |
|||
Tensile Strength at Break | >= 26.0 MPa @Temperature 23.0 °C |
>= 3770 psi @Temperature 73.4 °F |
ASTM D1708 |
Solvay Specialty Polymers Hyflon® PFA M620 Perfluoroalkoxy (PFA)
(Unverified Data**) Hyflon PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resista.. |
|||
Tensile Strength at Break | <= 26.0 MPa | <= 3770 psi | ISO/R527 |
Polykemi AB POLYfill PPH T5060 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 26.0 MPa | <= 3770 psi | ISO/R527 |
Polykemi AB POLYfill PPHC K8040 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 26.0 MPa | <= 3770 psi | ISO/R527 |
Polykemi AB POLYfill PPHC TS20040 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
Azdel SuperLite® SL551600-100 PP Resin Matrix / 55% Glass Fiber (4 mm Molded Thickness) AZDEL SuperLite® SL551600-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | >= 26.0 MPa @Strain >=100 % |
>= 3770 psi @Strain >=100 % |
ISO R527 |
Shanghai Ofluorine 9201 PVDF Pellets for cables Description: Excellent mechanical properties, heat resistance and flame resistance, PVDF for cable can bear high temperature, corrosive chemicals etc harsh working environment, which has low smoke, .. |