NOVA Chemicals Dylark® FG2500 High-Heat Styrenic Copolymer

Category Polymer , Thermoplastic , SMA Polymer , Styrene-Maleic Anhydride (SMA), Heat Resistant
Manufacturer NOVA Chemicals
Trade Name Dylark®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Dylark® FG2500 High-Heat Styrenic Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description and Features: Styrenic copolymer with high-heat resistance, high-impact strength and good toughness. Resins used in food grade sheet extrusion and injection molding applications. Microwavable ResinProcessing: Contact NOVA Chemicals technical personnel for processing assistance. Data presented here is based on test results from a limited number of samples and may change as additional manufacturing data is obtained.Availability: Available in boxes, truckloads, and railcars.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D 792
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D 955
Melt Flow 0.60 g/10 min

@Load 2.16 kg,
Temperature 230 °C
0.60 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 26.0 MPa
3770 psi
0.2 inches/minute; ASTM D 638
Tensile Strength, Yield 28.0 MPa
4060 psi
0.2 inches/minute; ASTM D 638
Elongation at Break 20 %
20 %
0.2 inches/minute; ASTM D 638
Tensile Modulus 2.07 GPa
300 ksi
0.2 inches/minute; ASTM D 638
Flexural Strength 57.0 MPa
8270 psi
at <5% Strain, flexural testing speed of 0.5 inches/minute; ASTM D 790
Flexural Modulus 2.14 GPa
310 ksi
Flexural testing speed of 0.5 inches/minute; ASTM D 790
Izod Impact, Notched 2.67 J/cm

@Thickness 3.17 mm
5.00 ft-lb/in

@Thickness 0.125 in
ASTM D 256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 107 °C

@Thickness 3.17 mm
225 °F

@Thickness 0.125 in
Annealed; ASTM D 648
Vicat Softening Point 123 °C

@Load 1.00 kg
253 °F

@Load 2.20 lb
Rate B; 120°C/min; ASTM D 1525