Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D412 |
Multibase TPSiV™ 1180-50D Thermoplastic Silicone Vulcanizate These materials are a novel family of TPV products based on cross-linked silicone rubber dispersed into various engineering thermoplastics. The dispersion of the silicone internal phase is produced.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | 50 mm/min; ISO 527 |
Polimeri Europa Edistir R 850E Polystyrene Super high impact polystyrene with good heat resistance. Designed for sheet extrusion and thermoforming of deep drawn containers even
diluted with high percentage of GP. Suitable for general injecti.. |
|||
Tensile Strength at Break | <= 24.0 MPa | <= 3480 psi | ISO/R527 |
Polykemi AB POLYfill PP CIP6015F Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 24.0 MPa | <= 3480 psi | ISO/R527 |
Polykemi AB POLYfill PP CIP6015F VTUV Polypropylene, Mineral Reinforced, Heat and UV Stabilized Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 24.0 MPa | <= 3480 psi | ISO/R527 |
Polykemi AB POLYfill PPC T10030 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 24.0 MPa | <= 3480 psi | ISO/R527 |
Polykemi AB POLYfill PPC T2020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ISO R 527 |
Fainplast Compounds RE 265/D Rigid PVC, Extrusion Semi-rigid furniture border |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ISO 527 |
FKuR Kunststoff Fibrolon® P 8540 Wood-Plastic Compound, Fiber Reinforced FIBROLON® are fiber reinforced compounds. Fibrolon® P 8540 has a polypropylene base. With the brand name of FIBROLON® FKuR has developed natural fiber reinforced compounds (Wood-Plastics-C.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | 50mm/min; ASTM D638 |
Kingfa FRHIPS-960 Flame Retardant Polystyrene Features:UL 94 V-0 @ 1.6mm, V-0 @ 3.2mmExcellent balance properties, Non-DPOGood heat stabilityColor tailor-made for clientApplications:Injection moldingGas assistant moldingPrinter and photocopier .. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D638 |
Ineos Styrenics 496N High-Impact Polystyrene Resin (NAFTA) Description: High-impact, lower flow grades for food packaging, dairy containers, lids, plates, appliance components and housings.Information provided by BASF.Ineos Styrenics purchased this product .. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ISO 527 |
Lubrizol Advanced Materials Pearlbond® 12C75 Thermoplastic Polyurethane Pearlbond® 12C75 is polyester-based thermoplastic polyurethane, supplied in form of colourless, translucent granules, combining hardness with excellent low-temperature flexibility and a low softe.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | 50mm/min; ASTM D638 |
Kingfa FRHIPS-930 Flame Retardant Polystyrene Features:UL 94 V-0 @ 1.6mm, 5VA @ 2.6mmNon-DPO, high UV stabilityExcellent heat stabilityExcellent electrical propertiesApplications:Injection moldingGas moldingPrinter, photocopier, fax machineElec.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | |
JPJ Technologies 8300B HDPE Blow Molding Information provided by JPJ Technologies |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | 50 mm/min, 1A; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND 19T1040 PP SABIC® PPcompound 19T1040 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding application.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON AX01706 ABS LNP* STAT-KON* AX01706 is a compound based on ABS containing proprietary fillers. Added feature of this grade is: Electrically Conductive. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY A30009 ABS LNP* STAT-LOY* A30009 is a compound based on ABS. Added features of this material include: Antistatic, Flame Retardant. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY A3000T ABS (Asia Pacific) LNP* Stat-loy* A3000T is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Stat-loy A3000Z ABS (Asia Pacific) LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for t.. |
|||
Tensile Strength at Break | >= 24.0 MPa | >= 3480 psi | |
Sibur SKN-33ASE Nitrile-Butadiene Rubber (NBR) For production of rubber and asbestos technical articles which are used as sets for automobile, air planes, different machines and equipment, agricultural, drilling, and polygraph machinery, as well.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ISO R 527 |
Silon Taborex TA 1117HD Chemically-Crosslinkable HDPE Compound TABOREX TA 1117 HD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a “SIOPLA.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP WX02869H Polyester, TP LNP THERMOCOMP* WX02869H is a compound based on Polyester, TP resin containing High Specific Gravity. Added features of this material include: High Impact. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D638 |
Eastman Eastar MN059 Copolyester Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar MN059 Copolyester is a medical gra.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D638 |
3D Systems VisiJet M100 3-D Printer Model Material The InVision SR (standard resolution) 3-D printer delivers key advantages compared to other 3-D modeling technologies — superior model quality, durable photopolymer materials, surface finish and fe.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM-D638 |
Braskem ML4400N LLDPE Rotomolding Polyethylene The resin ML4400N is a linear low-density polyethylene, 1-butene based, with high stiffness and an adequate balance of processability and environmental stress cracking resistance. It contains long t.. |
|||
Tensile Strength at Break | 24.0 MPa | 3480 psi | ISO R 527 |
Addiplast Addilene H 526 N30 Polypropylene Homopolymer Improved rigidity, high durabilityInformation provided by Addiplast. |
|||
Tensile Strength at Break | >= 24.0 MPa | >= 3480 psi | |
Beijing Evergrow Resources UHMW PE Bar Applications:Engineering manufacture:gear wheel, bearing bushes, sliding elements, chute liners, bunker liners, chain wear strip, guide strips and liners. The paper industry:suction box covers and g.. |
|||
Tensile Strength at Break | <= 24.0 MPa | <= 3480 psi | ISO/R527 |
Polykemi AB POLYfill PP 150ENH Polypropylene, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 24.0 MPa | <= 3480 psi | ISO/R527 |
Polykemi AB POLYfill PP HBK1501515 Polypropylene, Multifiller High Gloss Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 24.0 MPa | <= 3480 psi | ISO/R527 |
Polykemi AB POLYfill PPHC K9030 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | >= 24.0 MPa | >= 3480 psi | ISO R 527 |
Fainplast Compounds KL 50 Flexible PVC, Insulation for High Temperatures Lead Free Insulation for low thickness |