Silon Taborex TA 1117HD Chemically-Crosslinkable HDPE Compound
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Crosslinkable |
| Manufacturer | Silon |
| Trade Name | Taborex |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Silon Taborex TA 1117HD Chemically-Crosslinkable HDPE Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TABOREX TA 1117 HD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a “SIOPLAS-SYSTEMâ€. It is used for the production of multi-layer pipes for domestic hot and cold water, under floor heating and central heating application. It is designed to achieve best performance in single layer and co-extrusion products.Information provided by Silon
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.540 g/cc | 0.0195 lb/in³ | DIN 53466 |
| Density | 0.948 g/cc | 0.0342 lb/in³ | DIN 53479/ASTM D1505 |
| Volatiles | <= 0.10 % | <= 0.10 % | ITM-ZP 300CH 3-5-5/d |
| Melt Flow | 1.0 g/10 min @Load 5.00 kg, Temperature 190 °C |
1.0 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133/ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 24.0 MPa | 3480 psi | ISO R 527 |
| Elongation at Break | 450 % | 450 % | ISO R 527 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 160 - 170 °C | 320 - 338 °F | |
| Zone 2 | 170 - 180 °C | 338 - 356 °F | |
| Zone 3 | 170 - 190 °C | 338 - 374 °F | |
| Zone 4 | 170 - 190 °C | 338 - 374 °F | |
| Die Temperature | 190 - 220 °C | 374 - 428 °F | |
| Head Temperature | 200 - 210 °C | 392 - 410 °F | |
| Screw Cooling Temperature | 70.0 - 90.0 °C | 158 - 194 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Gel content (%) | 70 | EN 579 |
Users viewing this material also viewed the following:
- Ovation Polymers OpteSTAT™ NC PC 1020 Polycarbonate based Carbon Nanotube Compound
- SABIC Innovative Plastics Lexan® HF1140R PC (Asia Pacific)
- Gromax BTG25-FN09N1 Nylon 6 25% Glass Filled (Dry)
- Solvay Specialty Polymers Tecnoflon® PL 458 Fluoroelastomer
- Dow Corning SILASTIC® 7-4870 BIOMEDICAL GRADE LSR, KIT
- Fainplast Compounds GA 87/1 Flexible PVC, Flame Retardant Sheathing
- ConocoPhillips ANDEROL® AA-40 White Mineral Food Grade Oil, ISO Grade 150, SAE Grade 40
- Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 1/8"
Copyright © lookpolymers.com All Rights Reserved