SABIC Innovative Plastics LNP STAT-LOY A3000T ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY A3000T ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-loy* A3000T is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
| 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.800 % | 0.800 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Time 86400 sec |
0.0050 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0068 cm/cm @Time 86400 sec |
0.0068 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0090 cm/cm @Time 86400 sec |
0.0060 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0083 cm/cm @Time 86400 sec |
0.0083 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ASTM D638 |
| 24.0 MPa | 3480 psi | ISO 527 | |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
| 32.0 MPa | 4640 psi | ISO 527 | |
| Elongation at Break | 39.1 % | 39.1 % | ASTM D638 |
| 62.9 % | 62.9 % | ISO 527 | |
| Tensile Modulus | 1.14 GPa | 165 ksi | 1 mm/min; ISO 527 |
| 1.37 GPa | 199 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 41.0 MPa | 5950 psi | ASTM D790 |
| 42.0 MPa | 6090 psi | ISO 178 | |
| Flexural Modulus | 1.37 GPa | 199 ksi | ASTM D790 |
| 1.40 GPa | 203 ksi | ISO 178 | |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 118 µm/m-°C @Temperature -40.0 - 40.0 °C |
65.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 119 µm/m-°C @Temperature -40.0 - 40.0 °C |
66.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 112 µm/m-°C @Temperature -40.0 - 40.0 °C |
62.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 112 µm/m-°C @Temperature -40.0 - 40.0 °C |
62.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 °C | 178 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 80.0 °C @Thickness 3.20 mm |
176 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+9 - 1.00e+11 ohm | 1.00e+9 - 1.00e+11 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Quadrant EPP Proteus® PP Natural Co-Polymer Polypropylene (ASTM Product Data Sheet)
- Global TPO-65D TPO Grade
- GrafTech GRAFCELL® FFP-300 SERIES Flow Field Plate Graphite
- Isoflon TFM
- Teknor Apex Monprene® MP 1213A Thermoplastic Elastomer
- ScanTube FEP Tubing
- A. Schulman POLYBATCH™ Poly Off-White P90062PF Concentrate Based In Polypropylene
- Diamond Polymers NPP30-3500G Homopolymer Polypropylene Granules
- Solvay Engineered Polymers SEQUEL® E2200 TPO (discontinued **)
Copyright © lookpolymers.com All Rights Reserved