SABIC Innovative Plastics LNP THERMOCOMP WX02869H Polyester, TP

Category	Polymer , Thermoplastic , Polyester, TP
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP THERMOCOMP WX02869H Polyester, TP.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

LNP THERMOCOMP* WX02869H is a compound based on Polyester, TP resin containing High Specific Gravity. Added features of this material include: High Impact.

Physical Properties	Metric	English	Comments
Density	4.86 g/cc	0.176 lb/inÂ³	ASTM D792
	4.87 g/cc	0.176 lb/inÂ³	ISO 1183
Moisture Absorption	0.0400 %	0.0400 %	50% RH, 24 hrs; ASTM D570
	0.0600 %	0.0600 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ASTM D955
	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.011 cm/cm @Time 86400 sec	0.011 in/in @Time 24.0 hour	ASTM D955
	0.0111 cm/cm @Time 86400 sec	0.0111 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	24.0 MPa	3480 psi	ASTM D638
	27.0 MPa	3920 psi	ISO 527
Tensile Strength, Yield	26.0 MPa	3770 psi	ASTM D638
	27.0 MPa	3920 psi	ISO 527
Elongation at Break	11.1 %	11.1 %	ISO 527
	23.8 %	23.8 %	ASTM D638
Elongation at Yield	9.4 %	9.4 %	ISO 527
	13 %	13 %	ASTM D638
Tensile Modulus	1.78 GPa	258 ksi	1 mm/min; ISO 527
	1.82 GPa	264 ksi	50 mm/min; ASTM D638
Flexural Strength	42.0 MPa	6090 psi	ISO 178
	48.0 MPa	6960 psi	ASTM D790
Flexural Modulus	1.93 GPa	280 ksi	ISO 178
	2.03 GPa	294 ksi	ASTM D790
Izod Impact, Notched	1.01 J/cm	1.89 ft-lb/in	ASTM D256
Izod Impact, Unnotched	13.72 J/cm	25.70 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	10.0 kJ/mÂ²	4.76 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	84.0 kJ/mÂ²	40.0 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	9.00 J	6.64 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	14.0 J	10.3 ft-lb	Multiaxial Impact; ISO 6603

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	92.5 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	51.4 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	92.5 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	51.4 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	91.7 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	50.9 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	91.8 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	51.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	57.0 Â°C	135 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	66.0 Â°C @Thickness 3.20 mm	151 Â°F @Thickness 0.126 in	unannealed; ASTM D648