Polymer Property : Tensile Strength at Break = 27600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	190 MPa	27600 psi	ISO 527-2
Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stabi..
Tensile Strength at Break	190 MPa	27600 psi	ISO 527-1/-2
Lanxess DurethanÂ® AKV 30 GIT H2.0 900116 Nylon 66, 30% Glass Fiber PA 66, injection molding grade, 30% glass fibers, suitable for GIT (gas assisted technology), good surface finish, good heat-ageing resistance
Tensile Strength at Break	190 MPa	27600 psi	ISO 527-1/-2
Lanxess DurethanÂ® BKV 35 HTS 901510 Nylon 6, 35% Glass Fiber PA 6, injection molding grade, 35% glass fibers, very good heat-ageing resistance
Tensile Strength at Break	190 MPa	27600 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® A 218 V30 BK 34 NG PA66, 30% glass fiber, DRY Description: TECHNYLÂ® A 218 V30 Black 34 NG is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. The product is available in black color.Benefits: This p..
Tensile Strength at Break	190 MPa	27600 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® A 218 V30 PA66, 30% glass fiber, DRY Description: TECHNYLÂ® A 218 V30 is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. This product is available in natural and black colors.Benefits: The ..
Tensile Strength at Break	190 MPa	27600 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® A 218W V33 Natural T PA66, 33% glass fiber, DRY Description: TECHNYLÂ® A 218W V33 Nat T is a polyamide 66, reinforced with 33% of glass fiber, heat stabilized, for injection molding. This product is available in natural color.Benefits: The prod..
Tensile Strength at Break	190 MPa	27600 psi	ISO 527 Type 1A
Solvay TECHNYLSTARâ„¢ S 218 V30 PA6, 30% glass filled, DRY Description: TECHNYLSTARâ„¢ S 218 V30 is based on a patented high flow polyamide 6 resin (TechnylStar), heat stabilized, reinforced with 30% of glass fiber, for injection molding. This product is..
Tensile Strength at Break	190 MPa	27600 psi
SGL Carbon Group PANOXÂ® SA C063 EEA High performance oxidized textile fiber, Crimped staple fiber, For carbon/carbon and spinning PANOXÂ® is the industry standard when it comes to fire-retardant textile fibers. As an oxidized, thermally stabilized polyacrylonitrile (PAN) fiber that will not burn, melt, soften or drip, PANOX ..
Tensile Strength at Break	190 MPa	27600 psi	ISO 527
SABIC Innovative Plastics LNP Verton OV00A PPS (Asia Pacific) LNP* Verton* OV00A is a compound based on Polyphenylene Sulfide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break	190 MPa	27600 psi	ASTM D638
SABIC Innovative Plastics LNP VERTON PV007 PA 6 LNP* VERTON* PV007 is a compound based on Nylon 6 resin containing 35% Long Glass Fiber. Added feature of this grade is: Structural.
Tensile Strength at Break	190 MPa	27600 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® A 216 V30 PA66, 33% glass fiber, DRY Description: Polyamide PA66, reinforced with 30% of glass fiber, for injection molding.Available in: Asia Pacific, Europe, Latin America and North America Product Applications: TECHNYL A 216 V30 is ..
Tensile Strength at Break	190 MPa	27600 psi	ASTM D638
A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66 Information provided by A. Schulman.
Tensile Strength at Break	190 MPa	27600 psi	ASTM D638
A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66 Information provided by A. Schulman.
Tensile Strength at Break	190 MPa	27600 psi	ASTM D638
A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66 Information provided by A. Schulman.
Tensile Strength at Break	190 MPa	27600 psi	ISO 527-1/-2
DSM Akulon® S223-HG6 (Dry) 30% Glass Reinforced Nylon 66 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis..
Tensile Strength at Break	190 MPa	27600 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® BG-30 PA6-GF30 Product description: Grilon BG-30 is a heat stabilized PA6 injection molding grade with 30% glass fibers. Grilon BG-30 has the following important properties: High stiffnessGood balance between stre..
Tensile Strength at Break	190 MPa	27600 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® TSG-30/4 W PA666-GF30 Product description: Grilon TSG-30/4 W is a high heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 30% glass fibers, modified for parts with high thermal demands. Grilon TSG-..
Tensile Strength at Break	190 MPa	27600 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® TSG-35/4 H black 9836 PA666-GF35 Product description: Grilon TSG-35/4 H is a high heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 35% glass fibers, modified for parts with high thermal demands. Grilon TSG-..
Tensile Strength at Break	190 MPa	27600 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® TSG-35/4 W black 9832 PA666-GF35 Product description: Grilon TSG-35/4 W is a high heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 35% glass fibers, modified for parts with high thermal demands. Grilon TSG-..
Tensile Strength at Break	190 MPa	27600 psi	50%RH; ISO 527-1/-2
DuPont Performance Polymers Zytel® FG70G50HSLA BK309 Nylon 66 (Unverified Data**) 50% Glass Reinforced Heat Stabilized Polyamide 66 with Developed for Food Contact Applications Information provided by DuPont Performance Polymers
Tensile Strength at Break	190 MPa	27600 psi	50%RH; ISO 527-1/-2
DuPont Performance Polymers Zytel® HTN 51G35HSLR BK420 Polyphthalamide (PPA) (Unverified Data**) 35% Glass Reinforced PPA High Performance Polyamide Zytel HTN51G35HSLR BK420 is a 35% glass reinforced heat stabilized lubricated high performance polyamide resin with improved hydrolysis resistance..
Tensile Strength at Break	190 MPa	27600 psi	ISO 527-1/-2
DSM Stanyl® 46HF5040 Nylon 46-40% Glass Reinforced (European and Asian Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper..
Tensile Strength at Break	190 MPa	27600 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® LBV-65H FWA nat PA12-GF65 Product description: Grilamid LBV-65H FWA natural is a 65% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combined w..
Tensile Strength at Break	190 MPa	27600 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® XE 4216 black 9233 PA6T/66-GF30 Product description: Grivory XE 4216 black 9233 is a high heat stabilized, 30% glass fiber reinforced, semicrystalline, thermoplastic engineering material for injection molding. Polymer designation ..
Tensile Strength at Break	190 MPa	27600 psi	5 [mm/min]; ISO 527-1/2
Akro-Plastic Akromid® A3 GF 60 (2424) PA 6.6 Conditioned, 60% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat..
Tensile Strength at Break	190 MPa	27600 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® 70G30HSL BK039B Nylon 66 (Unverified Data**) 30% Glass Reinforced Heat Stabilized Polyamide 66 Information provided by DuPont Performance Polymers
Tensile Strength at Break	190 MPa	27600 psi
Radici Radilon® A RV330 (dry) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov..
Tensile Strength at Break	190 MPa	27600 psi	ISO 527
Solvay Specialty Polymers Ixef® 1313/0004 Polyarylamide, 40% Glass Fiber + Elastomer, DAM (discontinued **)&l Impact modified. The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manu..