Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 100 MPa | <= 14500 psi | ISO/R527 |
Polykemi AB SCANTEC PC S60R GF30 V0 Polycarbonate, Glass-Fiber Reinforced, Flame Retardant Information provided by Polykemi AB |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® BFL2015 PC (Asia Pacific) Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only |
|||
Tensile Strength at Break | 100 MPa @Thickness 4.00 mm, Temperature 23.0 °C |
14500 psi @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded; ISO 527-2/50 |
PolyOne Edgetek® ET3500-5002 BK Acrylonitrile Styrene Acrylate + PC (ASA+PC) The Edgetek™ Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for .. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® AKV 325 H2.0 901510 Nylon 66, 25% Glass Fiber PA 66, 25% glass fibers, extrusion- and blow molding grade, branched, high viscosity, good heat-ageing resistance, good hydrolysis resistance |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® BKV 30 EF 000000 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers, low viscosity (Easy Flow) |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 218C V10 PA66, 10% glass fiber, DRY Description: TECHNYL® A 218C V10 is a polyamide 66, reinforced with 10% of glass fiber, heat stabilized, for injection molding. This product is available in black color.Benefits: Due to specially.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 Type 1A |
Solvay TECHNYL® C 218 MZ20 V10 Black Z PA6, 20/10% mineral/glass fiber, DRY Description: Polyamide PA6, reinforced 20 % mineral filler and 10 % of glass fiber, heat stabilized, for injection molding.Available in: Asia PacificProduct Applications: TECHNYL C 218 MZ20 V10 offe.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 Type 1A |
Solvay TECHNYL® R AR 130/GF Nylon 66, 30% glass fiber, Conditioned Description: TECHNYL® AR 130/GF is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. It contains recycled raw materials. This product is available in bla.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
Techmer ES Electrafil® M-2426 BK Polycarbonate |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
UBE UBESTA® 3020GX9 23% Glass Fiber Reinforced Nylon 12 Description: UBE UBESTA® Automotive grade Nylon 12Comments: 23% glass fiber reinforced gradeInformation provided by UBE. |
|||
Tensile Strength at Break | 100 - 130 MPa | 14500 - 18900 psi | ISO 527 |
Vyncolit Vyntec® CF8030 Carbon Fiber Reinforced Novolac Phenolic Carbon fiber reinforced phenolic moldable composite with superior tribological properties. High tensile and flexural strength and modulus combined with low density.Information provided by Vyncolit,.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1 |
Vyncolit X655RB Glass Fiber and Mineral Filled Novolac Phenolic Novolac resin based, glass fiber and mineral reinforced. Grade with superior stiffness, high dimensional stability and high wear resistance. Good chemical resistance against several fuels at elevate.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6000 GV 25 HWUVCP 25% Glass Fiber Nylon 6, UV Stabilized, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 5026 (BG-30 H) PA6-GF30 Product description: Grilon B XE 5026 (BG-30 H) black 9922 is a high heat stabilized, 30% glass fiber reinforced PA6- Injection molding grade with modified flowability. Grilon B XE 5026 (BG-30 H) bl.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | |
Ensinger TECATRON™ PVX Polyphenylene sulfide (PPS), Bearing Grade TECATRON PPS is a high performance thermoplastic that combines good mechanical properties with excellent thermal and chemical resistance properties. There is no known solvent that dissolves TECATRON.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 |
Eurotec® Tecodur® PB70 GR15 BK002 XA21 PBT, 15% glass fiber reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 |
Eurotec® Tecodur® PB70 GR15 NL PBT 15% glass fiber reinforced Excellent stiffness and hardnessGood mechanical strengthGood creep and fatigue behaviorVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 |
Eurotec® Tecodur® PB70 GR30 NL XA60 PBT, 30% glass fiber reinforced, flame retardant - halogen & red phosphorus, heat stabilized, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 |
Eurotec® Tecopet® PT70 KK45 PET, 45% glass fiber/mineral reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | v = 5 mm/min; ISO 527-2 |
CENTROPLAST CENTROMID 6.6 GF 30 Polyamide 6.6 30% glass fiber This material has very high strength and rigidity, with lower moisture absorption. It can be used for housing parts, threaded bolts, and distance pieces.Information provided by CENTROPLAST Engineer.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 - 1 & - 2 |
Asahi Kasei Tenac®-C GN455 Copolymer Acetal Resin 25% Glass Fiber - filled, high-flow grade, with high stiffness and superior dimensional stabilityInformation provided by Asahi Kasei Corporation. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
Beijing Chemical Industry KAIFA® 301-G15F PBT Resin 15% glass fiber reinforced, flame retardant, good flow, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527-1,-2 |
Covestro Makroblend® UT4045 G PC/PBT Blend, 20% Glass Filled Main characteristics:• High toughness even at low temperatures• Good chemical resistance• Good paintability• Good flowability• Low moisture intakeGrade characteristics:• Excellent chemic.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 |
BASF Ultramid® B3WG6 GP BK 23210 30% Glass Filled PA6 (Conditioned) Description: 30% Glass fiber reinforced and heat aging resistant injection molding grade used e.g. for automobile manifold.Information provided by BASF |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
Beijing Chemical Industry KAIFA® MN201-G20 Nylon 66 Resin 20% glass fiber reinforced, thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 |
DSM Akulon® K-FKGS6 (Cond.) 30% Glass Reinforced Nylon 6 (North America)
(discontinued **) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
Tensile Strength at Break | 100 MPa | 14500 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® LC-15H black PA12-CF15 Product description: Grilamid LC-15H black is a Polyamide 12 injection molding product reinforced with 15% carbon fibers. The product is inherently black and is only available in this color.Main Att.. |