BASF Ultramid® B3WG6 GP BK 23210 30% Glass Filled PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3WG6 GP BK 23210 30% Glass Filled PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: 30% Glass fiber reinforced and heat aging resistant injection molding grade used e.g. for automobile manifold.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 6.3 - 6.9 % | 6.3 - 6.9 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.9 - 2.3 % | 1.9 - 2.3 % | 23°C; 50% RH; ISO 62 |
| Viscosity Measurement | 145 | 145 | ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 |
| Elongation at Break | 7.5 % | 7.5 % | ISO 527-1/-2 |
| Tensile Modulus | 5.60 GPa | 812 ksi | ISO 527-1/-2 |
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
| Flexural Modulus | 5.50 GPa | 798 ksi | ISO 178 |
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO 3146 |
| Maximum Service Temperature, Air | 200 °C | 392 °F | |
| Decomposition Temperature | >= 300 °C | >= 572 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat |
| Zone 1 | 260 °C | 500 °F | Feed Zone |
| Zone 2 | 270 °C | 518 °F | Compression |
| Zone 3 | 280 °C | 536 °F | Metering-zone |
| Zone 4 | 280 °C | 536 °F | Nozzle |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding/Extrusion |
| 280 °C | 536 °F | Optimal | |
| Mold Temperature | 80.0 °C | 176 °F | Optimal |
| 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal |
| <= 0.15 % | <= 0.15 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK 23210 | |
| Commercial Status | Europe | |
| Ignition Temperature | >400°C | ASTM D1929 |
| Peripheral screw speed | < 0.3 m/s |
Users viewing this material also viewed the following:
- Network Polymers NPS 90-0304 F Super High Impact Polystyrene
- Freudenberg Simrit V174 Fluoroelastomer Self-Lube
- Iran Petrochemical (PCC) 52518 High Density Polyethylene
- Haynes 625 alloy, 0% cold reduction
- SMAC SMACFOAM® 1250S-06 Damping Material
- Westlake Hifor SC74557 Linear Low Density Polyethylene
- Hexcel® HexWeb® CR III 1/16-5052-.0007 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Unipetrol Grade D Diesel Oil
- DSM Biomedical CarboSil® 20 80A Thermoplastic Silicone Polycarbonate Polyurethane (TSPCU)
- Axiall PURGOVIN® 3000 Rigid PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved