Solvay TECHNYL® C 218 MZ20 V10 Black Z PA6, 20/10% mineral/glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 218 MZ20 V10 Black Z PA6, 20/10% mineral/glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide PA6, reinforced 20 % mineral filler and 10 % of glass fiber, heat stabilized, for injection molding.Available in: Asia PacificProduct Applications: TECHNYL C 218 MZ20 V10 offers an excellent planarity of the end product, high mechanical properties and a high dimensional stability. This grade is commonly used in the automotive industry to mould large parts with a low warpage, such as: car body parts, engine covers, housings.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183/A |
| Linear Mold Shrinkage | 0.0057 cm/cm | 0.0057 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0054 cm/cm | 0.0054 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0095 cm/cm | 0.0095 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 Type 1A |
| Elongation at Break | 3.3 % | 3.3 % | ISO 527 Type 1A |
| Tensile Modulus | 7.40 GPa | 1070 ksi | ISO 527 Type 1A |
| Flexural Strength | 255 MPa | 37000 psi | ISO 178 |
| Flexural Modulus | 9.30 GPa | 1350 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180/1eA |
| Izod Impact, Unnotched (ISO) | 82.0 kJ/m² | 39.0 ft-lb/in² | ISO 180/1eU |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.41 J/cm² | 6.71 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 220 - 240 °C | 428 - 464 °F | |
| Front Barrel Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 230-250°C |
Users viewing this material also viewed the following:
- Nabaltec APYMAG® 80 Magnesium Hydroxide
- NOVA Chemicals Sclair® 2318 LLDPE Injection Molding Resin (discontinued **)
- DSM Biomedical PurSil® AL 20 Aliphatic Thermoplastic Silicone Polyether Urethane (discontinued **)
- MetalTek MTEK 25-12 TYPE II Cast UNS J93303 Heat Resistant Stainless Steel
- Mitsui MILEXâ„¢ RN-2830MB Acrylic Rubber Modified Phenolic Resin
- Silberline "A" Series A-226
- A. Schulman SCHULAMID® 6 GF15H 15% Glass Bead Reinforced, Heat Stabilized Nylon 6
- DuPont Performance Polymers Rynite® FG530 NC011 Polyethylene Terephthalate (PET) (Unverified Data**)
- CMW® 73 Copper Alloy
- BASF Polystyrol® 576 H Impact Grade Polystyrene (Europe)