Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 69.0 MPa | 10000 psi | ISO.527 DIN.53455 |
Omnia Plastica Akulon® POM h Acetal Homopolymer The general features of homopolymer acetalic resin are similar to those of copolymer POM c, except that service temperature (under load) is slightly higher but resistance to hydrolysis and strong al.. |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycolac® INP563 ABS+SAN SABIC INP563 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet.. |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 244R PC 10.5 MFR. Improved flame retardance. USA FDA compliant (limited colors). Internal mold release. |
|||
Tensile Strength at Break | 68.9 MPa | 10000 psi | ASTM D638 |
Polymer Resources PCSF-FR G30 Polycarbonate, 30% Glass Reinforced Structural Foam Grade Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel.. |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® FXD104R PC FXD104R is a Light Diffusion effect, which is part of the VisualFX family. Color Package may affect properties. |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® FXD104R PC (Europe-Africa-Middle East) FXD104R is a Light Diffusion effect, which is part of the VisualFX family. Color Package may affect properties.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® XHT4141 PC Copolymer (Europe-Africa-Middle East) XHT4141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® XHT4143 PC Copolymer (Asia Pacific) XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C. It is available in a range of opaque and limited transparent colors. |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | ISO 527 |
Polyplastic Armlen® PP GF MF 30-1 Polypropylene, 30% Glass and Mineral Filled Injection moldingInformation provided by PolyPlastic Group. |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Stat-kon RX89129 PA 66 LNP* Stat-Kon RX89129 is a compound based on Nylon 6,6. Fillers are proprietary.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 68.9 MPa | 10000 psi | ASTM D638 |
Techmer ES Plaslube® J-80/20/TF/15 BK223 Acetal (POM) Copolymer |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | ASTM D638 |
Sumitomo Bakelite Durez® 32245 Phenolic, Compression Grade Durez 32245 Black Phenolic is a two-stage glass fiber and mineral filled special purpose molding compound. It is especially designed for applications requiring high strength and dimensional stabilit.. |
|||
Tensile Strength at Break | 68.9 MPa | 10000 psi | |
Master Bond EP30HT-LO NASA Low Outgassing, Optically Clear Coating Description: Master Bond EP30HT-LO is a moderate viscosity, two component epoxy adhesive formulated to cure at room temperature or more rapidly at elevated temperatures, with a four to one mix ratio.. |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | ASTM D638 |
Unitika LM-8503-10 Chemical resistance, and excellent lubricant propertyInformation provided by Unitika Ltd. |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | ISO 527-2 |
Tisan TISLAMID® 6 15% Mineral Filled Flame Retardant (V0). Heat Stabilized Nylon 6 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec.. |
|||
Tensile Strength at Break | 68.9 MPa | 10000 psi | ASTM D638 |
Entec Hylex® P1010L2 HB Polycarbonate Available in North America Additive: Mold Release Features: Good Mold Release and Medium Flow RoHS Compliant Form: Pellets Appearance: Blue Information provided by Entec |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers PC 0614UV UV Stabilized Polycarbonate Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers PC 2418 R UV UV Stabilized/Mold Release Polycarbonate Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | 5 mm/min; ISO 527 |
Eurostar Starflam PK0022E PA6, 10% Mineral Filled, Injection Molded PK0022E is a Halogen Free and Phosphorous Free, Mineral Filed, Polyamide 6 Injection Molding (also known as PM3620Z22 or PA 10E6 U9 Z22)Information provided by Polymer Technology & Services, the Nor.. |
|||
Tensile Strength at Break | 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOTUF VX99810 Super Tough Nylon Super Tough Nylon, Proprietary Filler(s), |
|||
Tensile Strength at Break | 68.9 MPa | 10000 psi | 2.0 in/min; ASTM D638 |
LTL Color Compounds ColorFast® FRPC300 Polycarbonate, Flame-Retarded V2-rated polycarbonateAll information provided by LTL Color Compounders, Inc. |