Diamond Polymers PC 2418 R UV UV Stabilized/Mold Release Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, UV Stabilized |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers PC 2418 R UV UV Stabilized/Mold Release Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 28 g/10 min @Load 1.20 kg, Temperature 300 °C |
28 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 69.0 MPa | 10000 psi | chs 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Break | 132 % | 132 % | chs 2.0 in/min; ASTM D638 |
| Flexural Strength | 98.5 MPa | 14300 psi | chs 0.05 in/min; ASTM D790 |
| Flexural Modulus | 2.274 GPa | 329.8 ksi | chs 0.05 in/min; tangent; ASTM D790 |
| Izod Impact, Notched | 5.40 J/cm @Thickness 3.17 mm |
10.1 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 67.5 µm/m-°C @Temperature -40.0 - 93.3 °C |
37.5 µin/in-°F @Temperature -40.0 - 200 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | 0.125";; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C | 268 °F | 0.125";; ASTM D648 |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 105-71 RA Calcined Aluminum Oxide
- Polymax® Maxelast® P2955T TPE, PP Overmold or Standalone use
- Plastcom SLOVALEN PC 93 T 5 PP reinforced with 5% mineral filler
- PolyOne Edgetek® AS-03CF/000 Acrylonitrile Butadiene Styrene (ABS), Carbon Fiber Reinforced (discontinued **)
- Fujipoly Industries Sarcon® 15GHR Thin-Film GHR
- Trelleborg B500 Commercial Nitrile Rubber
- Cossa Polimeri ESTABLEND PA 3000 ABS / Nylon 6 Blend
- ChevronTexaco Meropa® 220
- 3M FM128 Indoor UL Recognized White Polyester Label Products
- 3M 4492W Double Coated Polyethylene Foam Tape
Copyright © lookpolymers.com All Rights Reserved