Unitika LM-8503-10
| Category | Polymer , Thermoplastic , Polyarylate |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika LM-8503-10.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Chemical resistance, and excellent lubricant propertyInformation provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Water Absorption | 0.13 % @Thickness 3.17 mm, Time 86400 sec |
0.13 % @Thickness 0.125 in, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0037 cm/cm @Thickness 3.00 mm |
0.0037 in/in @Thickness 0.118 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | ASTM D785 |
| Tensile Strength at Break | 69.0 MPa | 10000 psi | ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D638 |
| Flexural Strength | 109 MPa | 15800 psi | ASTM D790 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ASTM D790 |
| Compressive Strength | 86.0 MPa | 12500 psi | ASTM D695 |
| Izod Impact, Notched | 0.470 J/cm @Thickness 3.17 mm |
0.881 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Middle Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |
| Front Barrel Temperature | 250 - 270 °C | 482 - 518 °F | |
| Nozzle Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | actual surface temp |
| Drying Temperature | 100 °C | 212 °F | |
| Dry Time | 10.0 - 24.0 hour | 10.0 - 24.0 hour | |
| Back Pressure | 0.490 - 1.47 MPa | 71.1 - 213 psi | gage pressure |
Users viewing this material also viewed the following:
- NOVA Chemicals Gedexcel® 44XA Expandable Polystyrene
- Kennametal Stellite Tribaloy® T-900
- Momentive Performance Materials RTV6708 One-Component, Modified Alkoxy Adhesive Sealant, Translucent
- SABIC Innovative Plastics LNP LUBRICOMP WI001 PBT
- Universal Wire Works BAu-4 (AMS 4787) Gold Brazing Filler Metal
- A. Schulman POLYFORT™ FPP 1182 Talc Fortified Impact Resistant Polypropylene
- Austin Novel Materials Texalan® 298A Polyester-based TPU
- Anderman Ceramics EA999 Sintered Alumina, 99.9%
- DuPont Performance Polymers Minlon® 12T NC010 Nylon 66 (Unverified Data**)
- Ravago Manufacturing Americas Hylex® P1010G15 HB Polycarbonate, 15% Fiberglass Reinforced
Copyright © lookpolymers.com All Rights Reserved