Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 92.0 MPa | 13300 psi | ISO.527 DIN.53455 |
Omnia Plastica PEEK Polyetheretherketone Semicrystalline polymer. Material with high mechanical and thermal properties, up to 240°C. It resists to creep under load and to wear, its friction coefficient is low. The temperature resistance w.. |
|||
Tensile Strength at Break | 92.0 MPa @Temperature 23.0 °C |
13300 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Crastin® HR5315HF BK503 PBT
(Unverified Data**) Crastin® HR5315HF is a 15% glass reinforced PBT with high flow (HF), moderately toughened, hydrolysis resistant (HR) resin. Excellent balance of properties between terminal pullout and impact resis.. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | ISO 527 |
Nilit FRIANYL A63 K Nylon 6.6 for injection molding Nylon 6.6 for injection molding, formulated for the coloration of button baths.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | ISO 527 |
Nilit FRIANYL A63 KV40 Nylon 6.6 for injection molding, 40% glass ball reinforced Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | ISO 527-1/-2 |
Lanxess Pocan® KU 2-7209 Z 000000 PBT, 15% Glass Fiber PBT, 15% glass fibers, injection molding, flame retardant, impact modified |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | Conditioned; ISO 527 Type 1 A |
Solvay Technyl® A 60G1 V25 25% Glass Reinforced Nylon 66, Flame Retardant This Red Phosphorous and Halogen free flame retardant grade, combines excellent all-round mechanical properties with outstanding flame retardancy (UL 5VA at 1.6mm) and electrical performance. This p.. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | ISO 527 Type 1A |
Solvay TECHNYL® C 52G1 V20 PA6, DRY Description: Halogen and Red Phosphorous free fire resistant polyamide PA6 Glass reinforced for injection molding of thin walled partsAvailable in: Asia Pacific, Europe, Latin America and North Amer.. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem 2212 PEI 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem 2212 PEI (Asia Pacific) 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2212R PEI 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2212R PEI (Asia Pacific) 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Lubricomp ZFL24 PPO LNP* Lubricomp* ZFL24 is a compound based on Modified Polyphenylene Oxide (PPO) containing glass fiber and PTFE lubricant. Characteristics of this grade are: Internally Lubricated.This data was su.. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® CS815 PBT+PET 15% glass reinforced PBT+PET. Improved heat aged color stability, high surface gloss. Oven knobs and handles, kickplates, trim. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® V8030CS PBT+PET Glass filled Valox with enhanced surface |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP PH0400CX PA 6 LNP* THERMOCOMP* PH0400CX is a compound based on Nylon 6 resin. Added feature of this grade is: High Specific Gravity. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP PH0400CX_BK1D466 PA 6 4.0 specific gravity, Nylon 6 |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp WF006SXC PBT LNP* Thermocomp* WF006SXC is a compound based on PBT containing Glass FIber. Characteristic of this grade is: Heat Stabilized.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DX95523C PC LNP* STAT-KON* DX95523C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Verton NV0081EV_GY7E149 PC+ABS Preliminary data for 40% long fiber single pellet non-halogen FR color filled PC/ABSThis data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | ISO 527-1/-2 |
DuPont Performance Polymers Crastin® HR5315HF BK503 Polybutylene Terephthalate (PBT)
(Unverified Data**)& 15% Glass Reinforced Hydrolysis Resistant Polybutylene Terephthalate Crastin HR5315HF is a 15% glass reinforced PBT with high flow (HF) moderately toughened hydrolysis resistant (HR) resin. Excellen.. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Minlon® 10B40 NC010 Nylon 66
(Unverified Data**) 40% Mineral Reinforced Polyamide 66Minlon 10B40 NC010 is a 40% mineral reinforced polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | ASTM D638 |
Beijing Chemical Industry KAIFA® 301-G20 PBT Resin 20% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | ISO 527-93 |
Wellman Wellamid® MRB40K004-WT1 40% Mineral Reinforced Nylon 66 Description: Mineral Reinforced Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 92.0 MPa | 13300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP GFL36 PSU (Europe-Africa-Middle East) LNP* Lubricomp* GFL36 is a compound based on Polysulfone resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated. |